测试材料疲劳强度的试验方法技术
Test method for testing fatigue strength of materials
The invention relates to a test method for testing the fatigue strength of materials, which can efficiently measure the fatigue strength of materials through parallel tests. The invention divides a large number of specimens into several groups, and completes the test in parallel on different test machines. Graphic analysis and data processing are carried out on the stress value rising and falling diagrams of the resulting multi-group specimens, and the synthetic stress value rising and falling diagrams are obtained, and then the mean and variance of fatigue strength are obtained by conventional methods. It can be used in fatigue strength test of metal materials with large number of samples.
【技术实现步骤摘要】
测试材料疲劳强度的试验方法本申请是申请号为：201510263521.0，专利技术创造名称为《一种用于测试材料的疲劳强度的试验方法》，申请日为：2015年5月21日的专利技术专利申请的分案申请。
本专利技术涉及测量材料的疲劳强度极限数据处理领域，特别涉及一种用于疲劳强度测试的并行升降试验法。
技术介绍
材料在指定寿命下的疲劳强度通常无法直接测定。自从测定疲劳强度的升降法被提出以后，这种方法被广泛地应用于测定材料疲劳强度的随机特征，例如广泛所用的金属材料。传统的升降试验法一般采用如下的流程：（1）估计预定寿命下试件的疲劳强度。确定试验的起始应力水平和级差。通常参考已有的相关试验数据或预试验数据确定起始应力水平，而级差则取为所估计疲劳强度的5%。（2）在起始应力水平下进行疲劳寿命试验。（3）如果试件在预定寿命前发生了疲劳破坏。在此应力水平下记为“破坏”，下一个试件在低一级的应力水平下进行疲劳寿命试验。如果试件达到预定寿命仍未发生破坏，本试件的试验停止，在此应力水平下记为“溢出”，下一个试件在高一级的应力水平下进行疲劳寿命试验，每一个试件的试验都依赖前一个试件的试验结果...
【技术保护点】
1.一种测试材料疲劳强度的试验方法，其特征在于包括如下几个步骤：①根据测试试验的样品数分为M组，M≥2；②第1组试样，选择循环基数
【技术特征摘要】
1.一种测试材料疲劳强度的试验方法，其特征在于包括如下几个步骤：①根据测试试验的样品数分为M组，M≥2；②第1组试样，选择循环基数，应力比r，参考材料性质选择接近于材料估计的疲劳极限的应力值进行第1件试件的试验；若循环数达到选择基数前发生破坏，则在低一级应力水平下进行第2件的试验，若仍在循环数达到选择基数前发生破坏，则再降一级应力水平进行第3次试验，若经过选择基数循环未破坏，则停止第3件的试验，升高一级应力水平，即在第2件的应力水平下进行第4次试验；以此类推，可得到应力值升降图，升降图应满足闭合条件；③剩下的M-1组试样从第1组得到的有效应力值开始试验，选择相同的循环基数和应力比r，重复步骤②的操作，可得到应力值升降图；④对产生的M组试样的应力值升降图进行图形分析和数据处理，得到合成后的应力值升降图，再按常规方法求出疲劳强度的均值与方差；具体来讲：对产生的M组试样的应力值升降图进行图形分析和数据处理，得到合成后...
【专利技术属性】
技术研发人员：周金宇，陈峰，李仲树，
申请(专利权)人：江苏理工学院，
类型：发明
国别省市：江苏,32