The invention discloses a grooving stress releasing method for reinforcing ceramic tile and stone internal and external walls, which is characterized by the following steps: (1) opening stress releasing groove step; (2) treating stress separating groove interface step; (3) filling stress separating groove sealant step. The invention releases the temperature stress of the ceramic tile exterior wall and slows down the deformation of the wall surface by installing the vertical stress separating groove and the transverse stress separating groove on the ceramic tile exterior wall, filling the vertical stress separating groove and the transverse stress separating groove with sealant, sealing the vertical stress separating groove and the transverse stress separating groove.
【技术实现步骤摘要】
一种瓷砖石材内外墙加固的开槽释放应力工法
本专利技术涉及建筑内外墙瓷砖、石材加固
,特别涉及一种瓷砖外墙加固的开槽释放应力工法。
技术介绍
内外墙饰面粘贴瓷砖、石材、马赛克等材料属刚性材料，两种不同属性的材料的膨胀系数等技术性能指标差别较大。特别是传统工艺粘贴瓷砖用水泥素灰的砖缝，夏季气温达到35℃时，外墙保温层温度可高达70℃--80℃，突遇降雨瞬间气温可降为10℃--20℃，温差50℃--60℃。两种膨胀系数差别较大的两种材料粘结在一起，时而久之势必造成水泥素灰的瓷砖缝龟裂。冬季，下雪时雨水渗入裂缝中冻融后，就势必会出现瓷砖空鼓、脱落，造成砸死人、砸伤人的安全事故。严重的威胁到人居环境的安全。
技术实现思路
本专利技术所要解决的技术问题在于针对瓷砖、石材内外墙应力造成瓷砖外墙空鼓所存在的问题而提供一种瓷砖外墙加固的开槽释放应力工法。本专利技术所要解决的技术问题可以通过以下技术方案来实现：一种瓷砖、石材内外墙加固的开槽释放应力工法，包括如下步骤：(1)开应力释放分隔槽步骤该步骤中，首先在瓷砖外墙竖向每隔3-5m用切割机切割出一道竖向应力分隔槽，在瓷砖外墙水平方...
【技术保护点】
1.一种瓷砖、石材内外墙加固的开槽释放应力工法，其特征在于，包括如下步骤：(1)开应力释放分隔槽步骤该步骤中，首先在瓷砖外墙竖向每隔3‑5m用切割机切割出一道竖向应力分隔槽，在瓷砖外墙水平方向每层瓷砖用切割机切割出一道横向应力分隔槽，竖向应力分隔槽和横向应力分隔槽的宽度为10mm～20mm，深度10‑15mm；(2)应力分隔槽界面处理步骤在切割出的竖向应力分隔槽和横向应力分隔槽内涂刷补强界面剂加固外墙基层；(3)应力分隔槽嵌填密封胶步骤用密封胶填满竖向应力分隔槽和横向应力分隔槽并密封竖向应力分隔槽和横向应力分隔槽。
【技术特征摘要】
1.一种瓷砖、石材内外墙加固的开槽释放应力工法，其特征在于，包括如下步骤：(1)开应力释放分隔槽步骤该步骤中，首先在瓷砖外墙竖向每隔3-5m用切割机切割出一道竖向应力分隔槽，在瓷砖外墙水平方向每层瓷砖用切割机切割出一道横向应力分隔槽，竖向应力分隔槽和横向应力分...
【专利技术属性】
技术研发人员：杨雨奕，缪德忠，
申请(专利权)人：上海天补材料科技有限公司，
类型：发明
国别省市：上海,31