The invention discloses a high content calcium silicate filled polyethylene masterbatch, which is characterized in that the carrier is weighed by weight fraction: low density polyethylene 19-25 phr, coupling agent 0.3-0.7 phr, epoxy resin 0.2-0.8 phr, filling material: calcium silicate powder is filled with 75-80% of the total weight of carrier and additive. Silane coupling agent is used to activate calcium silicate powder, epoxy resin protective agent is added to restrain the loss of low molecular weight silane coupling agent during high temperature processing, eliminate or minimize the formation of bubbles, and ensure the performance of the product; on the other hand, the addition of epoxy resin can further improve the performance of the powder in the matrix. The dispersion of calcium silicate increases the filling content of calcium silicate and the interfacial effect between the powder and the matrix.
【技术实现步骤摘要】
一种高含量硅酸钙填充聚乙烯母粒及其制备方法
本专利技术涉及填充母粒的制备方法，尤其涉及一种高含量硅酸钙填充低密度聚乙烯母粒的制备方法。
技术介绍
聚乙烯作为应用最广的通用塑料之一，其塑料制品的生产在世界各地快速发展，应用领域也在日益扩大，从日常生活产品到工企业产品都能随处可见聚乙烯塑料制品。为了提高和改善其塑料制品的性能，一般采用加入填充母粒来改性的方法，具体操作是将粉体加入到聚乙烯基体中制成母粒，然后再稀释到产品中，此方法不仅可以实现功能上的改性，同时可以极大地降低材料成本，从来在日益激烈的市场竞争中脱颖而出。在现有技术中为了改善相关粉体在基体中的分散性，通常需要将粉体进行活化处理，一般用偶联剂对粉体进行表面处理，偶联剂的存在能够一定程度上改善粉体在基体中的分散状况，然而要想填充高含量的粉体，偶联剂的分散作用存在一定的局限性，同时偶联剂作为低分子量物质，在后期的高温加工过程中容易损耗，从而产生气泡在产品上形成微孔甚至是孔洞，这将会对产品的性能造成较大的负面影响。
技术实现思路
本专利技术要解决的技术问题是：解决低分子量偶联剂易损耗且改善分散性存在局限性的问题，提供一...
【技术保护点】
1.一种高含量硅酸钙填充聚乙烯母粒，其特征在于：按重量分数称取载体：低密度聚乙烯19～25份，偶联剂：0.3～0.7份，环氧树脂：0.2～0.8份，填充料：硅酸钙粉体填加量为载体和添加剂总重的75～80％。
【技术特征摘要】
1.一种高含量硅酸钙填充聚乙烯母粒，其特征在于：按重量分数称取载体：低密度聚乙烯19～25份，偶联剂：0.3～0.7份，环氧树脂：0.2～0.8份，填充料：硅酸钙粉体填加量为载体和添加剂总重的75～80％。2.根据权利要求1所述的一种高含量硅酸钙填充聚乙烯母粒，其特征在于：所述偶联剂为硅烷偶联剂为γ-氨丙基三乙氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅烷和γ-(甲基丙烯酰氧)丙基三甲氧基硅烷中的一种。3.根据权利要求1所述的一种高含量硅酸钙填充聚乙烯母粒，其特征在于：所述环氧树脂为双酚Α型环氧树脂。4.根据权利要求1所述的一种高含量硅酸钙填充聚乙烯母粒，其特征在...
【专利技术属性】
技术研发人员：张纯，任粒，刘伟，罗源，吴显，
申请(专利权)人：贵州理工学院，
类型：发明
国别省市：贵州,52
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。