一种硅烷甲醛吸附材料及其制备方法技术

本发明专利技术公开了一种硅烷甲醛吸附材料及其制备方法，该硅烷甲醛吸附材料是由下述重量份的原料组成的：硅烷偶联剂kh550 1‑3、饱和十八碳酰胺2‑3、蜂蜡10‑13、纳米碳粉100‑123、丙酸钙2‑4、N‑月桂酰肌氨酸钠1‑3、四氢糠醇3‑5。本发明专利技术将纳米碳粉采用饱和十八碳酰胺水溶液分散，然后采用硅烷偶联剂kh550改性，有效的提高了吸附材料的表面活性，增强了对甲醛的吸附效果。

Silane formaldehyde adsorption material and preparation method thereof

The invention discloses a silane formaldehyde adsorbent material and a preparation method thereof. The silane formaldehyde adsorbent material is composed of the following weight components: silane coupling agent KH550 1_3, saturated octadecanamide 2_3, beeswax 10_13, nanometer carbon powder 100_123, calcium propionate 2_4, sodium lauroyl creatine 1_3, tetrahydrofurfuryl alcohol 3. 5. The nanometer carbon powder is dispersed by saturated octadecanamide aqueous solution, and then modified by silane coupling agent kh550, which effectively improves the surface activity of the adsorption material and enhances the adsorption effect on formaldehyde.

【技术实现步骤摘要】
一种硅烷甲醛吸附材料及其制备方法
本专利技术属于吸附材料领域，具体涉及一种硅烷甲醛吸附材料及其制备方法。
技术介绍
室内甲醛、苯等有害气体作为家居生活中不可避免的隐性杀手，时刻威胁人们的身体健康。而这些有害气体的释放是一个缓慢的过程，即使再好的空气净洁产品，也不可能一次性、彻底净化空气，因此如何能够更高效的去除甲醛，是目前研究的重点。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种硅烷甲醛吸附材料及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种硅烷甲醛吸附材料，它是由下述重量份的原料组成的：硅烷偶联剂kh5501-3、饱和十八碳酰胺2-3、蜂蜡10-13、纳米碳粉100-123、丙酸钙2-4、N-月桂酰肌氨酸钠1-3、四氢糠醇3-5。所述硅烷甲醛吸附材料的制备方法，包括以下步骤：（1）取硅烷偶联剂kh550，加入到其重量5-7倍的无水乙醇中，搅拌均匀，升高温度为60-65℃，加入四氢糠醇，保温搅拌10-20分钟，得复合醇分散液；（2）取饱和十八碳酰胺、纳米碳粉混合，加入到混合料重量13-20倍的去离子水中，搅拌均匀，得碳粉溶液；（3）取蜂蜡，加入到其重本文档来自技高网...

【技术保护点】
1.一种硅烷甲醛吸附材料，其特征在于，它是由下述重量份的原料组成的：硅烷偶联剂kh550 1‑3、饱和十八碳酰胺2‑3、蜂蜡10‑13、纳米碳粉100‑123、丙酸钙2‑4、N‑月桂酰肌氨酸钠1‑3、四氢糠醇3‑5。

【技术特征摘要】
1.一种硅烷甲醛吸附材料，其特征在于，它是由下述重量份的原料组成的：硅烷偶联剂kh5501-3、饱和十八碳酰胺2-3、蜂蜡10-13、纳米碳粉100-123、丙酸钙2-4、N-月桂酰肌氨酸钠1-3、四氢糠醇3-5。2.一种如权利要求1所述硅烷甲醛吸附材料的制备方法，其特征在于，包括以下步骤：（1）取硅烷偶联剂kh550，加入到其重量5-7倍的无水乙醇中，搅拌均匀，升高温度为60-65℃，...

【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：安徽中弘科技发展有限公司，
类型：发明
国别省市：安徽,34