The present invention relates to a degreasing composition. The degreasing composition is composed of degreasing powder and degreasing agent. The degreasing powder is composed of 80_95 wt% anhydrous sodium metasilicate and 5_20 wt% water. The degreasing agent is composed of 10_30 wt% surfactant and 70_90 wt% water. The compound is dissolved in 100 parts water and the mass ratio of degreasing powder to degreasing agent in the degreasing composition is 1:0.5_1.8. By using only sodium metasilicate and surfactant, the invention can achieve high efficiency degreasing of the workpiece, and can realize long-term non-replacement of degreasing agent even without organic solvents such as alcohols and ethers.
【技术实现步骤摘要】
一种去油脂组合物
本专利技术涉及一种去油脂组合物。
技术介绍
由于钢铁工件在制造时所采用的防腐蚀措施、加工过程中的污染，钢铁工件表面必定有油污附着。陈克忠先生在《金属表面防腐蚀工艺》中提出钢铁工件表面挂油量应小于0.2g/m2，否则将影响磷化膜的生成，从而影响涂装的质量，因此，在钢铁表面涂装前的处理中必须采用脱脂剂去除钢铁表面的油污。脱脂剂，按操作方法可分为浸渍脱脂剂、喷淋脱脂剂、擦试脱脂剂等；按操作温度可分为高温脱脂剂（80～90℃）、中温脱脂剂（50～70℃）、低温脱脂剂（30～50℃）、常温脱脂剂（10～40℃）；按组成可分为有机溶剂脱脂剂、乳液脱脂剂、化学脱脂剂等类型。化学脱脂剂又可分为水基脱脂剂、酸性脱脂剂、碱液脱脂剂等。水基脱脂剂一般由表面活性剂、碱、助洗剂等组成，利用表面活性剂等对油脂的乳化、分散、增溶等作用，除去工件表面的皂化性和非皂化性油脂；利用碱性物质与皂化性油脂的皂化反应，使不溶于水的皂化性油脂变成能溶于水的阴离子表面活性剂肥皂及甘油，皂化反应在pH值＞8.5时进行，温度越高，反应越快；其中，碱性物质包括氢氧化钠、偏硅酸钠、碳酸钠等。常温水基...
【技术保护点】
1.一种去油脂组合物，其特征在于，所述去油脂组合物由脱脂粉和脱脂剂组成，所述脱脂粉由80‑95wt%的无水偏硅酸钠以及5‑20wt%的水组成，所述脱脂剂由10‑30wt%的表面活性剂以及70‑90wt%的水组成，所述去油脂组合物使用时将4.5‑20重量份的去油脂组合物溶解于100重量份的水中，所述去油脂组合物中脱脂粉和脱脂剂的质量比为1：0.5‑1.8。
【技术特征摘要】
1.一种去油脂组合物，其特征在于，所述去油脂组合物由脱脂粉和脱脂剂组成，所述脱脂粉由80-95wt%的无水偏硅酸钠以及5-20wt%的水组成，所述脱脂剂由10-30wt%的表面活性剂以及70-90wt%的水组成，所述去油脂组合物使用时将4.5-20重量份的去油脂组合物溶解于100重量份的水中，所述去油脂组合物中脱脂粉和脱脂剂的质量比为1：0.5-1.8。2.根据权利要求1所述的一种去油脂组合物，其特征在于，所述表面活性剂为阴离子表面活性剂。3.根据权利要求1所述的一种去油脂组合物，其特征在于，所述表面活性剂为磺酸盐阴离子表面活性剂。4.根据权利要求1所述的一种去油脂组合物，其特征在于，所述表面活性剂为十二烷基苯磺酸盐表面活性剂。5.根据权利要求1所述的一种去油脂组合物，其特征在于，所述脱脂粉还包括1-5wt%柠檬醛羧甲基改性壳聚糖。6.一种去油脂组合物的应用方法，其特征在于，包括以下步骤：将待脱脂工件在预脱脂槽中进行常温预脱脂20min后进行水洗，得到预处理工件，所述预脱脂槽中含有4.5-20重量份的去油脂组合物以及10...
【专利技术属性】
技术研发人员：杨年富，
申请(专利权)人：湖州富美材料科技有限公司，
类型：发明
国别省市：浙江,33