The present invention relates to a method for improving the wear resistance of high entropy alloy, in which the high purity metal sample is melted under the protection of argon in vacuum arc furnace: the master alloy ingot with uniform composition is obtained by repeated melting; the master alloy ingot is obtained by copper mold suction casting method; and the remelted state obtained by repeated smelting and suction casting of the sample is obtained. High entropy alloy. The hardness and wear resistance of the high entropy alloy prepared by the invention after remelting treatment are obviously improved to meet the performance requirements of key wear-resistant parts of agricultural machinery, and can be widely used in high-end agricultural machinery, and can also be applied in other areas with high wear resistance requirements.
【技术实现步骤摘要】
一种提高高熵合金耐磨性能的方法
本专利技术涉及一种提高高熵合金耐磨性能的方法。
技术介绍
高熵合金是由至少五种及五种以上金属元素按照等原子比或接近等原子比的方法混合而成,形成组织单相或两相的固溶体合金。高熵合金是近几年研究开发出来的一种新型材料,具有优异的力学性能和广泛的应用前景,受到越来越多的重视。高熵合金具有高耐磨性、高耐腐蚀性、优异的热稳定性、高强度、高硬度和抗高温氧化性等优异特性。这些优良的性能满足了农业机械关键的性能要求,可在高端农业机械上得到广泛应用。目前对于高熵合金的研究主要集中在成分和热处理对高熵合金的组织结构和性能的影响上,对于利用热历史改善高熵合金性能的研究很少,尤其是重熔处理对高熵合金耐磨性的影响。
技术实现思路
为了解决上述问题,本专利技术提供了一种提高高熵合金耐磨性能的方法,能显著提高高熵合金耐磨性能。一种提高高熵合金耐磨性能的方法,步骤如下:1、将高纯金属试样放在真空电弧熔炼炉内在氩气保护下熔炼:首先抽真空至2×10-3Pa,然后充入氩气至气压为0.06-0.08MPa,打开电流,熔化金属试样,熔炼完金属试样后,再持续进行电磁搅拌熔炼10秒 ...
【技术保护点】
1.一种提高高熵合金耐磨性能的方法,其特征在于:步骤如下:1)将高纯金属试样放在真空电弧熔炼炉内在氩气保护下熔炼:首先抽真空至2×10‑3Pa,然后充入氩气至气压为0.06‑0.08MPa,打开电流,熔化金属试样,熔炼完金属试样后,再持续进行电磁搅拌熔炼10秒钟,冷却,用搅拌棒将其翻转,按照上述条件进行第二次熔炼;2)按照步骤1)反复熔炼至少四次,得到成分均匀的母合金锭;3)将母合金锭通过铜模吸铸法得到所需要的试样;4)将步骤3)获得的试样表面进行打磨,除去表面的氧化膜,放到无水乙醇中超声波清洗机震荡5分钟,除去表面多余残渣;然后重新放到真空电弧炉坩埚内熔炼:重复步骤1)‑ ...
【技术特征摘要】
1.一种提高高熵合金耐磨性能的方法,其特征在于:步骤如下:1)将高纯金属试样放在真空电弧熔炼炉内在氩气保护下熔炼:首先抽真空至2×10-3Pa,然后充入氩气至气压为0.06-0.08MPa,打开电流,熔化金属试样,熔炼完金属试样后,再持续进行电磁搅拌熔炼10秒钟,冷却,用搅拌棒将其翻转,按照上述条件进行第二次熔炼...