The invention relates to the technical field of polymer materials, in particular to a low temperature impact resistant PC/ABS composite material and its products. The low temperature impact resistant PC/ABS composite material comprises components: silicone copolymerized PC resin, ABS resin, toughening agent, flame retardant and inorganic filler. The products are products produced after molding PC/ABS composites with low temperature impact resistance. The low temperature impact resistant PC/ABS composite material of the invention can have excellent notch impact strength after adding inorganic filler and at low temperature by adding organosilicon copolymerized PC and composite toughening agent resistant to low temperature impact.
【技术实现步骤摘要】
耐低温冲击PC/ABS复合材料及其产品
本专利技术涉及高分子材料
，具体地说是一种耐低温冲击PC/ABS复合材料及其产品。
技术介绍
PC/ABS复合材料广泛应用在家用电器、汽车等领域，具有易加工成型、物性可调节范围宽等优点。为了提高PC/ABS复合材料的模量，通常在PC/ABS复合材料中加入无机填料，但加入无机填料后的缺口冲击强度严重下降，尤其是在低温情况下的缺口冲击强度，，如-20℃时，这对PC/ABS复合材料的应用造成了严重限制。有鉴于此，实有必要开发一种耐低温冲击PC/ABS复合材料，以解决现有技术中PC/ABS复合材料在加入无机填料后缺口冲击强度严重下降的问题。
技术实现思路
因此，本专利技术的目的是提供一种耐低温冲击PC/ABS复合材料，在加入无机填料后、在低温的情况下，具有优异的缺口冲击强度。为了达到上述目的，本专利技术的耐低温冲击PC/ABS复合材料，其按重量份数表示，包括：(1)有机硅-共聚PC树脂即A成分20-60份；(2)ABS树脂即B成分，所述A成分和B成分的重量份数比在1.5-9.5之间；(3)增韧剂即C成分3-7份，所述增...
【技术保护点】
1.一种耐低温冲击PC/ABS复合材料，其特征在于，按重量份数表示，包括：(1)有机硅‑共聚PC树脂即A成分20‑60份；(2)ABS树脂即B成分，所述A成分和B成分的重量份数比在1.5‑9.5之间；(3)增韧剂即C成分3‑7份，所述增韧剂为复配增韧剂；(4)阻燃剂即D成分5.5‑13份；(5)无机填料即E成分5‑40份。
【技术特征摘要】
1.一种耐低温冲击PC/ABS复合材料，其特征在于，按重量份数表示，包括：(1)有机硅-共聚PC树脂即A成分20-60份；(2)ABS树脂即B成分，所述A成分和B成分的重量份数比在1.5-9.5之间；(3)增韧剂即C成分3-7份，所述增韧剂为复配增韧剂；(4)阻燃剂即D成分5.5-13份；(5)无机填料即E成分5-40份。2.根据权利要求1所述的耐低温冲击PC/ABS复合材料，其特征在于，在温度300℃、负重1.2Kg时，所述A成分的熔体质量流动速率为3-70g/10min之间。3.根据权利要求1所述的耐低温冲击PC/ABS复合材料，其特征在于，所述耐低温冲击PC/ABS复合材料还包括除有机硅-共聚PC之外的PC树脂即F成分0.1-60份。4.根据权利要求3所述的耐低温冲击PC/ABS复合材料，其特征在于，所述F成分为双酚A型聚碳酸酯、聚酯型聚碳酸酯、环己烷双酚A型聚碳酸酯、双酚TMC合成的耐高温聚碳酸酯中的至少一种。5.根据权利要求3或4所述的耐低温冲击PC/ABS复合材料，其特征在于，在温度300℃、负重1.2Kg时，所述F成分的熔体质量流动速率为3-70g...
【专利技术属性】
技术研发人员：马海丰，
申请(专利权)人：汉达精密电子昆山有限公司，
类型：发明
国别省市：江苏,32