The invention discloses a pretreatment method which can enhance the dyeing performance of aramid toward anionic dyes. The pretreatment solution is prepared by dissolving N_n-butyl phthalimide, cationic gelatin protein auxiliaries and sodium hydroxide into water in step 1. A certain amount of aramid tow is prepared in step 2. The invention can significantly improve the dyeing performance of aramid fiber to anionic dyes, and provides a new way for solving the difficult dyeing problem of aramid fiber and developing the dyeing of aramid anionic dyes, realizing the atmospheric pressure dyeing of aramid fiber at 100 C, lowering the dyeing temperature and reducing the dyeing rate. Cost and pollution, promote the development and application of aramid products.
【技术实现步骤摘要】
一种能够增强芳纶对阴离子染料染色性能的预处理方法
本专利技术属于纺织品印染方法
，涉及一种能够增强芳纶对阴离子染料染色性能的预处理方法。
技术介绍
芳纶是一种芳香环的聚酰胺合成纤维，已工业化的芳纶主要是芳纶1313(聚间苯二甲酰间苯二胺纤维)和芳纶1414(聚对苯二甲酰对苯二胺纤维)两大类。芳纶纤维具有高强、高模、耐高温、耐辐射、电绝缘性、阻燃性、热湿舒适性和化学性稳定性好等优良性能。芳纶材料应用广泛，除了应用于高温过滤材料、电器绝缘材料、蜂巢结构材料和防火材料等外，还能应用于特种服装材料，如航天服、消防服、赛车服、油田工作服等特殊用途的高性能纺织品。由此引起芳纶染色产品越来越受到人们的重视。然而，芳纶是由酰胺键互相连接苯基所构成的线型大分子。芳纶大分子结构十分紧密，分子中含有大量酰胺基和芳香环，分子间氢键多，内聚力大，纤维溶胀困难，结晶度高，玻璃化温度高，间位芳纶玻璃化温度高达270℃，对位芳纶玻璃化温度高达350℃，且芳纶分子结构中不含水溶性基团，因此芳纶存在染色困难、得色量低、很难染深浓色的问题。而通常芳纶采用分散染料和阳离子染色时，染色温度高达140...
【技术保护点】
1.一种能够增强芳纶对阴离子染料染色性能的预处理方法，其特征在于，按照下述步骤进行：步骤1，配置预处理液：将N‑正丁基邻苯二甲酰亚胺、阳离子明胶蛋白助剂和氢氧化钠溶入水中，制得预处理液；步骤2，将一定量的芳纶投入步骤1得到的预处理液中，进行预处理。
【技术特征摘要】
1.一种能够增强芳纶对阴离子染料染色性能的预处理方法，其特征在于，按照下述步骤进行：步骤1，配置预处理液：将N-正丁基邻苯二甲酰亚胺、阳离子明胶蛋白助剂和氢氧化钠溶入水中，制得预处理液；步骤2，将一定量的芳纶投入步骤1得到的预处理液中，进行预处理。2.根据权利要求1所述的一种能够增强芳纶对阴离子染料染色性能的预处理方法，其特征在于，所述预处理液中，N-正丁基邻苯二甲酰亚胺的浓度为30g/L-50g/L，阳离子明胶蛋白助剂的浓度为10g/L-30g/L，氢氧化钠的浓度为4g/L-10g/L。3.根据权利要求1所述的一种能够增强芳纶对阴离子...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。