The invention discloses a flame retardant and bacteriostatic 3D printing material and a preparation method thereof. The 3D printing material comprises the following components by weight: ABS resin 80 112, 3_aminopropyl triethoxysilane 10 20, magnesium acetate 11 17, dodecyl gallate 13 18, monochlorotriazine beta cyclodextrin 5 11, 1,4 Naphthalic acid 1 5. The thermal insulation 3D printing material of the invention not only has the advantages of good bacteriostatic effect, high fireproof and flame retardant performance, but also is safer to use; the thermal insulation 3D printing material of the invention has small thermal conductivity, good thermal insulation effect, good mechanical performance, long service life and high market popularization value.
【技术实现步骤摘要】
一种阻燃抑菌的3D打印材料及其制备方法
本专利技术涉及一种3D打印材料，具体是一种阻燃抑菌的3D打印材料及其制备方法。
技术介绍
3D打印技术是制造业领域的一项新兴技术，有着巨大的发展前景，但是耗材却成了目前制约3D打印技术广泛应用的关键因素，而保温材料作为3D打印耗材的一种，更是有待发掘。3D打印常用材料有尼龙玻纤、耐用性尼龙材料、石膏材料、铝材料、钛合金、不锈钢、镀银、镀金、橡胶类材料。目前，保温材料主要分为有机保温材料和无机保温材料，相比于有机保温材料，无机保温材料的导热系数偏大，保温效果较差，但是防火阻燃、机械性能较好，而且使用寿命长；有机保温材料的导热系数小，保温效果良好，但是易燃烧，一旦发生火灾，会加快火势蔓延，并伴有大量毒气排出。另外，现有的保温材料抑菌效果差，使用安全性低。综上所述，有机保温材料和无机保温材料各有利弊。因此，本专利技术提供一种低导热系数、机械性能好、防火阻燃且抑菌的3D打印材料。
技术实现思路
本专利技术的目的在于提供一种阻燃抑菌的3D打印材料及其制备方法，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种...
【技术保护点】
1.一种阻燃抑菌的3D打印材料，其特征在于，所述3D打印材料包括以下重量份数的组分：ABS树脂80‑112份、3‑氨丙基三乙氧基硅烷10‑20份、乙酸镁11‑17份、没食子酸十二酯13‑18份、一氯三嗪‑β‑环糊精5‑11份、1,4‑萘二甲酸1‑5份。
【技术特征摘要】
1.一种阻燃抑菌的3D打印材料，其特征在于，所述3D打印材料包括以下重量份数的组分：ABS树脂80-112份、3-氨丙基三乙氧基硅烷10-20份、乙酸镁11-17份、没食子酸十二酯13-18份、一氯三嗪-β-环糊精5-11份、1,4-萘二甲酸1-5份。2.根据权利要求1所述的阻燃抑菌的3D打印材料，其特征在于，所述3D打印材料包括以下重量份数的组分：ABS树脂98份、3-氨丙基三乙氧基硅烷12份、乙酸镁14份、没食子酸十二酯15份、一氯三嗪-β-环糊精8份、1,4-萘二甲酸2份。3.一种如权利要求1-2任一所述的阻燃抑菌的3D打印材料的制备方法，其特征在于，包括以下步骤：(1)将乙酸镁和一氯三嗪-β-环糊精混合，加入混合物质量1-3倍的水，混合而均匀，得到混合物一；(2)将没食子酸十二酯与其2-3倍质量的65％的乙醇溶液混合，搅拌均匀，得到混合物二；(3)将混合物一与3-氨丙基三乙氧基硅烷混合，置于115-120℃下搅拌混合15-25min，得到混合物三；(4)将1,4-萘二甲酸与混合物二混合，置于60-70℃下搅拌混合40-50min，得到混合物四；(5)将混合物三与混合物四混合，置115-125℃下搅拌混合30-40min，得到混合物五；(6)将A...