一种聚合物太阳能电池阳极修饰层材料及制备方法技术

本发明专利技术涉及一种聚合物太阳能电池阳极修饰层材料及制备方法，所述的制备方法为：2,6‑二溴‑4,4‑双[1‑(磺酸钾)丁基]二噻吩并环戊二烯与4,4‑二硼酸‑2,6‑二氟联苯进行偶联反应，制得本发明专利技术聚合物太阳能电池阳极修饰层材料聚{4,4‑双[1‑(磺酸钾)丁基]二噻吩并环戊二烯‑交替‑2,6‑二氟联苯}。本发明专利技术制备的阳极修饰层材料用于聚合物太阳能电池阳极修饰，具有厚度不敏感的特点。

Polymer anode material for solar cell and preparation method thereof

The invention relates to a polymer solar cell anode modification layer material and a preparation method thereof. The preparation method is as follows: 2,6_dibromo_4,4_bis [1(potassium sulfonate) butyl] dithiophenylcyclopentadiene and 4,4_diboric acid_2,6_difluorobiphenyl are coupled to produce the polymer solar cell anode modification layer material of the invention. Poly ({4,4 [1 two) (potassium sulfonic acid) butyl] thiophene and cyclopentadiene alternating 2,6 2,6 fluorophenyl}}. The anode modification layer material prepared by the invention is used for the anode modification of polymer solar cells, and has the characteristics of insensitive thickness.

【技术实现步骤摘要】
一种聚合物太阳能电池阳极修饰层材料及制备方法
本专利技术涉及一种聚合物太阳能电池阳极修饰层材料及制备方法，具体属于光伏材料

技术介绍
聚合物太阳能电池具有无毒、柔性、低重量、低成本的优点，具有广阔的发展前景。聚合物太阳能电池一般由阳极、阳极修饰层材料、活性层、阴极修饰层材料、阴极组成。其中，阳极修饰层材料可以调控阳极的功函数，降低阳极与活性层之间的界面能力，提高聚合物太阳能电池的光电转换效率。目前聚合物太阳能电池常用的阳极修饰层材料是PEDOT:PSS。但是，PEDOT:PSS呈强酸性，会腐蚀电极，严重影响聚合物太阳能电池的稳定性。最近有文献和专利报道，使用中性的共轭聚电解质材料作为聚合物太阳能电池阳极修饰层材料，比如CPE-K、PCP-Na、PCPDT-T、CPEPh-Na、PhNa-1T等。共轭聚电解质阳极修饰层材料虽然解决了PEDOT:PSS腐蚀电极难题，但其存在电导率低的显著缺点。共轭聚电解质用于阳极修饰层时，必须加工的特别薄，厚度一般小于10纳米。共轭聚电解质用于阳极修饰层时，厚度超过10纳米，聚合物太阳能电池的光电转换效率会随共轭聚电解质厚度的增加而迅速衰减，存本文档来自技高网...

【技术保护点】
1.一种聚合物太阳能电池阳极修饰层材料及制备方法，其特征在于：所述的聚合物太阳能电池阳极修饰层材料的结构式如下：

【技术特征摘要】
1.一种聚合物太阳能电池阳极修饰层材料及制备方法，其特征在于：所述的聚合物太阳能电池阳极修饰层材料的结构式如下：所述的制备方法为：向反应釜内加入1.0摩尔2,6-二溴-4,4-双[1-(磺酸钾)丁基]二噻吩并环戊二烯、1.5摩尔4,4-二硼酸-2,6-二氟联苯和50.0毫升二甲基亚砜，通过鼓泡的方式，以1.0升/分钟的流速通入氮气1.0小时，并在氮气保护下，再加入0.04~0...

【专利技术属性】
技术研发人员：徐海涛，袁峰，唐玲璞，段一雄，刘俊，
申请(专利权)人：南昌航空大学，
类型：发明
国别省市：江西,36