The invention discloses an anti-aging PVC material and its preparation method. The material is made of the following components: PVC 100_150 weight parts, di-octyl terephthalate 30_50 weight parts, zinc stearate 0.2_0.5 weight parts, calcium stearate 0.2_0.5 weight parts, modified 4A zeolite 0.6_1 weight parts. The preparation method comprises the following steps: adding each component into a high-speed mixer according to the proportion, stirring speed 1200 rpm 1500 rpm, heating the material to 90 120 C, placing the material in a cold mixer, stirring speed 100 RPM 200 rpm, cooling the material below 50 C with cooling water. The PVC material of the invention has remarkable aging resistance and thermal stability without affecting other comprehensive properties such as flame retardancy, low cost and simple preparation method, and is especially suitable for industrial production.
【技术实现步骤摘要】
一种抗老化PVC材料及其制备方法
本专利技术属于化工
，涉及一种抗老化的PVC材料及其制备方法。
技术介绍
聚氯乙烯，英文简称PVC(Polyvinylchloride)，是氯乙烯单体(vinylchloridemonomer,简称VCM)在过氧化物、偶氮化合物等引发剂；或在光、热作用下按自由基聚合反应机理聚合而成的聚合物。氯乙烯均聚物和氯乙烯共聚物统称之为氯乙烯树脂。PVC为无定形结构的白色粉末，支化度较小，相对密度1.4左右，玻璃化温度77～90℃，170℃左右开始分解，对光和热的稳定性差，在100℃以上或经长时间阳光曝晒，就会分解而产生氯化氢，并进一步自动催化分解，引起变色，物理机械性能也迅速下降，在实际应用中必须加入稳定剂以提高对热和光的稳定性。目前在进行PVC材料加工时，需要加入抗老化剂以增强其抗老化性能，常规使用的抗老化剂有水滑石，剂量在10％以上。但是PVC材料中加入抗老剂有时会导致其他性能的降低，而且水滑石价格较高，性价比较差。
技术实现思路
本专利技术克服上述不足之处，提供一种综合性能强，成本低，制备方法简单，特别是无需额外加入抗老化剂还能具有...
【技术保护点】
1.一种抗老化的PVC材料，其特征在于该材料是由以下重量份的组分制成：PVC 100‑150重量份对苯二甲酸二辛酯 30‑50重量份硬脂酸锌 0.2‑0.5重量份硬脂酸钙 0.2‑0.5重量份改性4A沸石 0.6‑1重量份。
【技术特征摘要】
1.一种抗老化的PVC材料，其特征在于该材料是由以下重量份的组分制成：PVC100-150重量份对苯二甲酸二辛酯30-50重量份硬脂酸锌0.2-0.5重量份硬脂酸钙0.2-0.5重量份改性4A沸石0.6-1重量份。2.根据权利要求1所述的抗老化的PVC材料，其特征在于该材料是由以下重量份的组分制成：PVC100重量份对苯二甲酸二辛酯50重量份硬脂酸锌0.3-0.4重量份硬脂酸钙0.3-0.4重量份改性4A沸石0.6-0.8重量份。3.根据权利要求1或2所述的抗老化的PVC材料，其特征在于所述的改性4A沸石是将高氯酸缓慢均匀地喷洒到4A沸石表面，且边加边搅拌，高氯酸与4A沸石反应，高氯酸与4A沸石的重量比例是1：5-20。4.根...
【专利技术属性】
技术研发人员：印鑫，赵勇，
申请(专利权)人：常州佑佳新材料科技有限公司，
类型：发明
国别省市：江苏,32