本发明专利技术涉及一种太阳能电池用空穴传输材料及制备方法，其制备方法为：9‑[1‑(磺酸钠)丁基]‑2,7‑二溴咔唑与2,7‑双(4,4,5,5‑四甲基‑1,3,2‑二氧杂硼烷‑2‑基)‑9,9‑二辛基芴进行铃木偶联反应，获得太阳能电池用空穴传输材料聚{9‑[1‑(磺酸钠)丁基]‑2,7‑咔唑‑交替‑9,9‑二辛基芴}。本发明专利技术制备的空穴传输材料用于太阳能电池，具有加工容易、室温水醇溶液加工、中性、光电转换效率高等优点。

Hole transporting material for solar cell and preparation method thereof

The present invention relates to a hole transport material for solar cells and a preparation method thereof. The preparation method is as follows: 9[1(sodium sulfonate) butyl]2,7_dibromocarbazole and 2,7_bis (4,4,5,5_tetramethyl_1,3,2_dioxaborane_2_2-dioctyl fluorene are coupled to obtain the hole transport of solar cells by Suzuki coupling reaction. Materials: poly {9 ([1) (sodium sulfonate) butyl] 2,7 2,7 carbazole two, octyl fluorene}. The hole transmission material prepared by the invention is used for solar cells, and has the advantages of easy processing, room temperature water and alcohol solution processing, neutrality and high photoelectric conversion efficiency.

【技术实现步骤摘要】
一种太阳能电池用空穴传输材料及制备方法
本专利技术涉及一种太阳能电池用空穴传输材料及制备方法，具体属于有机太阳能电池用界面层材料

技术介绍
有机太阳能电池具有成本低、质量轻、可大面积加工、柔性好、应用领域广等优点，具有光明的应用前景。有机太阳能电池用空穴传输材料对其光电转换效率和稳定性有重要影响。空穴传输材料可以防止活性层与电极发生反应，从而提高有机太阳能电池的稳定性。空穴传输材料可以提高空穴的收集以及传输效率，调整活性层与电极间的界面势垒，从而提高有机太阳能电池的光电转换效率。目前有机太阳能电池常用的空穴传输材料是PEDOT∶PSS。但是，PEDOT∶PSS具有强酸性，会腐蚀电极，不利于有机太阳能电池的长期稳定。另外，PEDOT∶PSS具有强吸湿性，容易吸收空气中的水分，不利于有机太阳能电池的稳定性。此外，PEDOT∶PSS的空穴传输各向异性也不利于空穴的传输和手机，不利于有机太阳能电池的光电转换效率。目前有文献和专利报道使用共轭聚电解质材料作为有机太阳能电池的空穴传输层材料，比如PCP-Na、PFS、CPE-K、CPEPh-Na、PhNa-1T等。但是，上述共轭聚电解质本文档来自技高网...

【技术保护点】
1.一种太阳能电池用空穴传输材料及制备方法， 其特征在于：所述的太阳能电池用空穴传输材料的结构式如下：

【技术特征摘要】
1.一种太阳能电池用空穴传输材料及制备方法，其特征在于：所述的太阳能电池用空穴传输材料的结构式如下：所述的制备方法如下：向反应釜内加入1.0摩尔9-[1-(磺酸钠)丁基]-2,7-二溴咔唑、1.0摩尔2,7-双(4,4,5,5-四甲基-1,3,2-二氧杂硼烷-2-基)-9,9-二辛基芴、0.05摩尔四三苯基膦钯和50.0毫升二甲基亚砜，通过鼓泡的方式，以0.6升/分钟的流速通入氮气1.0...

【专利技术属性】
技术研发人员：徐海涛，符祥，张意晨，曾光，
申请(专利权)人：南昌航空大学，
类型：发明
国别省市：江西,36