The invention discloses a cement-based slag soil concrete, which is prepared from waste building slag soil, cement, stone, sand, water and water reducing agent. The composition of the mass percentage is as follows: cement: slag soil: water: sand: stone: 1:0.1:0.4:2:3.2, water reducing agent dosage according to 0.7% of the total quality of cement and slag soil, water cement ratio is 0.4; the invention aims to absorb waste engineering slag soil, replaces part of cement with waste engineering slag soil, through reasonable composition combination and scientific technology. A kind of cement-based slag-soil concrete with better strength was prepared. Compressive strength was increased by 8%-10% compared with traditional mixing method.
【技术实现步骤摘要】
一种水泥基渣土混凝土的制备工艺
本专利技术涉及一种混凝土制备技术，特别是涉及一种水泥基渣土混凝土制备工艺，属于建筑材料
技术介绍
建筑渣土一般是指在建筑工程、装饰工程、修复和养护工程的过程中所产生的建筑垃圾和工程渣土，渣土带来的危害包括污染路面、空气、水体、侵占土地和影响景观等。当前，建筑渣土的主要处理方式是填埋和作为道路路基填料。但是依然有大量的建筑废弃渣土因无法满足回填条件被遗弃，严重影响环境安全和人们的正常生活。实现建筑废弃渣土的变废为宝，对经济、生态环境及生态安全等都有着十分重要的实际意义。常见的建筑渣土，如水泥基渣土混凝土，的处理方式是将渣土碾成粉末状之后再掺入其他成分进行改良再使用，但碾磨渣土的生产成本非常高，给建筑渣土的再利用带来了一定困难。本专利技术人通过改变制备工艺的方式，在不对建筑废弃渣土进行磨粉处理的前提下，利用建筑渣土制备出一种抗压强度较高的水泥基渣土混凝土。一方面将废弃建筑渣再利用土，减少废弃建筑渣土排放量，减少其对环境的破坏，同时还能大大降低再利用的生产成本，提高生产效率。
技术实现思路
本专利技术基于消纳废弃建筑渣土、变废物为资...
【技术保护点】
1.一种水泥基渣土混凝土，以废弃建筑渣土、水泥、石子、砂、水、减水剂制备而成，其特征在于其质量百分比组成为：水泥:渣土:水:砂:石子为1:0.1:0.4:2.2:3.2，减水剂掺量为水泥和渣土质量总和的0.7％，水灰比为0.4；所述水泥为不低于P.O42.5；所述海沙的细度模数2.9，堆积密度1360kg/m3，表观密度2690kg/m3；所述石子的粒径为5～25mm，堆积密度为1451kg/m3,表观密度为2680kg/m3；所述减水剂为聚羧酸减水剂，减水率35％；采用水为本地自来水。
【技术特征摘要】
1.一种水泥基渣土混凝土，以废弃建筑渣土、水泥、石子、砂、水、减水剂制备而成，其特征在于其质量百分比组成为：水泥:渣土:水:砂:石子为1:0.1:0.4:2.2:3.2，减水剂掺量为水泥和渣土质量总和的0.7％，水灰比为0.4；所述水泥为不低于P.O42.5；所述海沙的细度模数2.9，堆积密度1360kg/m3，表观密度2690kg/m3；所述石子的粒径为5～25mm，堆积密度为1451kg/m3,表观密度为2680kg/m3；所述减水剂为聚羧酸减水剂，减水率35％；采用水为本地自来水。2.一种如权利要求1所述水泥基渣土混凝土制品的制备工艺，其特征在于包括以下步骤：1)按前述水泥基渣...
【专利技术属性】
技术研发人员：王海良，赵于博，荣辉，张磊，王雪平，杨久俊，
申请(专利权)人：天津城建大学，
类型：发明
国别省市：天津,12