The invention discloses a shotcrete admixture, which comprises the following weight components: water retaining agent 10_15 phr, polyvinyl alcohol 15_20 phr, water reducing agent 11_15 phr, polypropylene fiber 1_2 phr, cement accelerator 58_62 phr, active montmorillonite 3_20 phr, accelerator 10_25 phr, acrylic acid copolymer 1_12 phr, sodium nitrite 1_2 phr. 2 phr, 50_80 phr of expanded ultra-fine silica fume and 1_50 phr of calcium hydroxide can be sprayed normally on the surface of common seepage rock, which greatly reduces the seepage phenomenon of rock surface; the water-reducing effect is more than 30%, the 28-day strength can be increased to 50 MPa, and C40 anti-corrosion shotcrete can be prepared, which can fully solve the problem of rock burst and water-rich area shotcrete.
【技术实现步骤摘要】
一种喷射混凝土外加剂
本专利技术涉及外加剂
，尤其涉及一种喷射混凝土外加剂。
技术介绍
20世纪初，德国开发应用喷射混凝土砂浆支护巷道，20世纪50年代初，简易喷射机和速凝剂的研究成功，为喷射混凝土技术的应用创造了条件。到20世纪80年代，喷射混凝土技术已由过去的单一干喷发展到潮喷、湿喷、水泥裹砂喷射混凝土、钢纤维喷射混凝土等多种形式。实践证明，喷射混凝土同现浇混凝土相比，施工简便易行，省去支模、浇注和拆模工序，使混凝土输送、浇注和捣实合为一道工序，节省了人力，缩短了工期，还可以通过输料软管在高室或狭小工作区间的薄壁结构施工。目前，混凝土喷射技术已广泛应用于冶金、煤炭、水利及各种地下工程硐室、巷道的支护。但是，回弹率高、喷射质量不稳定是长期困扰喷射混凝土发展的难题。在实际施工操作中，喷射混凝土回弹率一般在30％以上，有的甚至超过40％，造成材料浪费，还影响工程质量和施工进度。
技术实现思路
鉴于此，本专利技术提供了一种喷射混凝土外加剂，包含以下重量份的组分，保水剂10-15份、聚乙烯醇15-20份、减水剂11-15份、聚丙烯纤维1-2份、水泥速凝剂58-62份、活性蒙脱土3-20份、速凝剂10-25份、丙烯酸共聚物1-12份、亚硝酸钠1-2份、膨化超细硅粉50-80份、氢氧化钙1-50份。对本专利技术的进一步描述，所述保水剂为冷水速溶型粉状甲基纤维素醚或冷水速溶型粉状羟乙基纤维素醚，所述聚乙烯醇为冷水速溶型粉状聚乙烯醇，所述的减水剂为萘系粉状减水剂。对本专利技术的进一步描述，所述粉剂塑化剂为聚羧酸系高性能减水剂，聚羧酸系减水剂固含量为97％-98％。采用...
【技术保护点】
1.一种喷射混凝土外加剂，其特征在于，包含以下重量份的组分，保水剂10‑15份、聚乙烯醇15‑20份、减水剂11‑15份、聚丙烯纤维1 ‑2份、水泥速凝剂58‑62份、活性蒙脱土3‑20份、速凝剂10‑25份、丙烯酸共聚物1‑12份、亚硝酸钠1‑2份、膨化超细硅粉50‑80份、氢氧化钙1‑50份。
【技术特征摘要】
1.一种喷射混凝土外加剂，其特征在于，包含以下重量份的组分，保水剂10-15份、聚乙烯醇15-20份、减水剂11-15份、聚丙烯纤维1-2份、水泥速凝剂58-62份、活性蒙脱土3-20份、速凝剂10-25份、丙烯酸共聚物1-12份、亚硝酸钠1-2份、膨化超细硅粉50-80份、氢氧化钙1-50份。2.根据权利要求...
【专利技术属性】
技术研发人员：张旋，
申请(专利权)人：徐州巨龙新材料科技有限公司，
类型：发明
国别省市：江苏,32