The invention relates to a method for burning environmental protection brick with fly ash, wherein the raw material for burning environmental protection brick with fly ash comprises the following components: fly ash: 50 80%; domestic garbage: 1 5%; cement: 5 15%; water: 5 9.6%; accelerator gypsum: 1 3%; activator silica fume: 0.1 0.5%; reduction. Water agent: 0.1, 0.5%; foaming stabilizer, chlorate: 0.5 1%. The process of the invention is simple, the density of the product is 300-700 kg/m3, and the strength is 2.5-7 MPa. The product meets the national quality requirements, and can be used as either non-load-bearing wall brick or external wall load-bearing brick. The invention realizes harmless treatment of industrial waste at lower cost, and has good economic and social benefits.
【技术实现步骤摘要】
一种利用粉煤灰烧制环保砖的方法
本专利技术涉及一种利用粉煤灰烧制环保砖的方法，特别是利用粉煤灰制成的环保砖，属于绿色建材制造领域。
技术介绍
粉煤灰是燃煤电厂排出的经静电集尘器收集得到的物质。燃煤形成的灰渣中粉煤灰约占4/5,底灰约占1/5。依据煤源及种类不同,形成的粉煤灰有显著差异。我国是以煤炭为主要能源的国家，电力的76％由煤炭产生，燃煤产生的粉煤灰总堆存量已超过10亿t，而且还在以每年0.8亿～1亿t的速度增加，成为世界上最大的排灰国[1]。粉煤灰存放不仅占用大量土地，还会造成严重的环境污染。开展粉煤灰等煤系固体废弃物综合利用，延伸煤炭产业链，不仅关系到中国煤炭产业、电力工业及相关工业可持续发展问题，而且对保护土地资源，减少、消除污染，实现循环经济具有重要意义。
技术实现思路
本专利技术的目的在于，提供一种利用粉煤灰烧制环保砖的方法。本专利技术的环保砖既可作非承重墙砖,也可作外墙承重砖，同时，操作相对简单，减少了人员和成本的投入，且利用粉煤灰或者生活垃圾作为原料在很大程度上降低了固体垃圾对环境的污染。本专利技术一种环保砖，它是由原料水泥、赤泥或废渣料、和助剂配制...
【技术保护点】
1.一种利用粉煤灰烧制环保砖的方法，其特征在于，是由原粉煤灰、生活垃圾、水泥、水、促凝剂石膏、活性剂硅灰、发泡稳定剂、减水剂氯酸盐组成，在每lOOKg原料中，、促凝剂石膏0.8～1.OKg,促凝剂石膏0.9～1.lKg、活化剂硅灰0.9～1.lKg发泡稳定剂18～20Kg,其余为水泥、粉煤灰或生活垃圾，水泥与粉煤灰或生活垃圾的质量比1:1。
【技术特征摘要】
1.一种利用粉煤灰烧制环保砖的方法，其特征在于，是由原粉煤灰、生活垃圾、水泥、水、促凝剂石膏、活性剂硅灰、发泡稳定剂、减水剂氯酸盐组成，在每lOOKg原料中，、促凝剂石膏0.8～1.OKg,促凝剂石膏0.9～1.lKg、活化剂硅灰0.9～1.lKg发泡稳定剂18～20Kg,其余为水泥、粉煤灰或生活垃圾，水泥与粉煤灰或生活垃圾的质量比1:1。2.如权利要求1所述的一种利用粉煤灰烧制环保砖的方法，其制备...
【专利技术属性】
技术研发人员：司传华，
申请(专利权)人：遵义联合建材有限公司，
类型：发明
国别省市：贵州,52