The invention provides a heating method for high-nickel steel ingots. The ingots are heated by a chamber furnace, and the ingots are loaded at the first heating stage t1: the furnace temperature is 200 C, then the furnace temperature is slowly raised to 700 C at a heating rate not higher than 40 C/h, and the first holding stage t2:700 C is kept for 4 - 6 h. In the second heating stage, the ingot is heated rapidly from 700 C to 900 C at the rate of 50 70 C / h, and in the second holding stage, the ingot is kept at 900 C for 4 6 h. In the third heating stage, the ingot is heated from 900 C to 1150 C at the rate of 30 40 After adopting the heating process of the invention, the heating effect of the high nickel steel ingot is good, and the surface crack defect is not found.
【技术实现步骤摘要】
一种高镍钢钢锭的加热方法
本专利技术属于热轧板带加热工艺
，特别涉及一种Ni≥10wt％的高镍钢钢锭的加热方法。
技术介绍
高镍钢是一种适用于超低温的低碳马氏体钢，由于其优异的超低温机械性能和良好的焊接性能，广泛应用于LNG储运设备建造。根据高镍钢的热塑性曲线，高镍钢在加热过程中存在两个脆性区，在脆性区内钢锭极易开裂。高镍钢第一脆性区位于700～900℃范围内，第二脆性区位于1180～1300℃范围内，与普通碳钢及合金钢的热塑性曲线大为不同，因此普通碳钢及合金钢钢锭的加热工艺并不适用于高镍钢钢锭。
技术实现思路
本专利技术旨在提供一种可避免高镍钢钢锭加热过程中出现开裂现象，保证钢锭加热质量的高镍钢钢锭的加热方法。为此，本专利技术所采取的技术解决方案是：一种高镍钢钢锭的加热方法，钢锭采用室式炉进行加热，依据高镍钢的热塑性曲线制定的加热工艺为：第一升温阶段t1：炉温200℃时钢锭装炉，随后炉温缓慢升温至700℃，升温速率不高于40℃/h；第一保温阶段t2：700℃保温4～6h。第二升温阶段t3：钢锭由700℃快速升温至900℃，升温速率50～70℃/h，快速通过高镍...
【技术保护点】
1.一种高镍钢钢锭的加热方法，其特征在于，对于Ni≥10wt％的高镍钢钢锭采用室式炉进行加热，依据高镍钢的热塑性曲线制定的加热工艺为：第一升温阶段t1：炉温200℃时钢锭装炉，随后炉温缓慢升温至700℃，升温速率不高于40℃/h；第一保温阶段t2：700℃保温4～6h；第二升温阶段t3：钢锭由700℃快速升温至900℃，升温速率50～70℃/h，快速通过高镍钢第一脆性区；第二保温阶段t4：在900℃保温4～6h；第三升温阶段t5：钢锭由900℃升温至1150℃，升温速率30～40℃/h：第三保温阶段t6：在1150℃保温5～7h，保证钢锭受热均匀；炉温不得超过1180℃，避...
【技术特征摘要】
1.一种高镍钢钢锭的加热方法，其特征在于，对于Ni≥10wt％的高镍钢钢锭采用室式炉进行加热，依据高镍钢的热塑性曲线制定的加热工艺为：第一升温阶段t1：炉温200℃时钢锭装炉，随后炉温缓慢升温至700℃，升温速率不高于40℃/h；第一保温阶段t2：700℃保温4～6h；第二升温阶段t3：钢锭由700℃...
【专利技术属性】
技术研发人员：张坤，丛津功，王若刚，李新玲，乔馨，张紫茵，于峰，杨军，李黎明，刘立强，
申请(专利权)人：鞍钢股份有限公司，
类型：发明
国别省市：辽宁,21