镓酸盐红色荧光粉、镓酸盐封装微晶玻璃制备方法技术

本发明专利技术公开了一种镓酸盐红色荧光粉、镓酸盐封装微晶玻璃制备方法，所述镓酸盐红色荧光粉以CaCO3、ZnO、MnCO3、Ga2O3为原料，通过高温固相法合成：Ca14Zn6Ga9.85O35:0.15Mn4+（1100oC,1150oC,1200oC,1250oC;4h,5h,6h,7h）系列红色荧光粉，所述原料的配比根据Ca14Zn6Ga9.85O35:0.15Mn4+称取配置；本发明专利技术的优点是发光效率高、热稳定性好、抗光衰性能好且可被蓝光有效激发。

Preparation of gallium red phosphor and gallium salt encapsulated glass ceramics

The invention discloses a preparation method of gallate red phosphor and gallate encapsulated glass-ceramics. The gallate red phosphor is synthesized by high-temperature solid-state method with CaCO3, ZnO, MnCO3 and Ga2O3 as raw materials: Ca14Zn6Ga9.85O35:0.15Mn4+ (1100oC, 1150oC, 1200oC, 1250oC; 4h, 5h, 6h, 7h) series of red phosphors. According to the Ca14Zn6Ga9.85O35:0.15Mn4+ weighing configuration, the material proportion has the advantages of high luminous efficiency, good thermal stability, good light fading resistance and can be effectively excited by blue light.

【技术实现步骤摘要】
镓酸盐红色荧光粉、镓酸盐封装微晶玻璃制备方法
本专利技术涉及一种微晶玻璃，具体是指镓酸盐红色荧光粉、镓酸盐封装微晶玻璃及其制备方法。
技术介绍
白光发光二极管(LED)作为一种新型的固态照明光源，由于其具有节能、环保、寿命长和可靠性高等优点而被誉为21世纪的绿色光源。目前市场上最为常用的荧光粉是有蓝光激发的黄色荧光粉YAG:Ce3+。但由于缺少红色成分，用这种荧光粉做成的LED存在显色指数偏低，色温偏高，偏冷白光等问题。这些问题严重限制了LED在诸多领域的使用与推广。因此，开发出高效，可靠的红色荧光粉成了当务之急。此外，微晶玻璃和荧光粉的导热性不够好，导致器件温度很高，常将器件烧坏。
技术实现思路
本专利技术的目的是为了克服现有技术存在的缺点和不足，而提供一种发光效率高、热稳定性好、抗光衰性能好且可被蓝光有效激发的镓酸盐红色荧光粉。本专利技术的第二个目的是提供一种镓酸盐封装微晶玻璃的制备方法。为实现上述第一个专利技术目的，其技术方案是所述镓酸盐红色荧光粉以CaCO3、ZnO、MnCO3、Ga2O3为原料，通过高温固相法合成分子式为Ca14Zn6Ga9.85O35:0.15Mn4+的红色荧本文档来自技高网...

【技术保护点】
1.一种镓酸盐红色荧光粉，其特征在于：所述镓酸盐红色荧光粉以CaCO3、ZnO、MnCO3、Ga2O3为原料，通过高温固相法合成分子式为Ca14Zn6Ga9.85O35:0.15Mn4+的红色荧光粉，所述原料的配比根据Ca14Zn6Ga9.85O35:0.15Mn4+称取配置。

【技术特征摘要】
1.一种镓酸盐红色荧光粉，其特征在于：所述镓酸盐红色荧光粉以CaCO3、ZnO、MnCO3、Ga2O3为原料，通过高温固相法合成分子式为Ca14Zn6Ga9.85O35:0.15Mn4+的红色荧光粉，所述原料的配比根据Ca14Zn6Ga9.85O35:0.15Mn4+称取配置...

【专利技术属性】
技术研发人员：向卫东，刘志聪，梁晓娟，
申请(专利权)人：温州大学，
类型：发明
国别省市：浙江,33