The invention provides a method of preparing polyamide conductive fiber by ultrasonic infiltration method, including the following steps: 1) the nylon 6 monofilament is used as raw material, and after washing to dry; 2) under the action of ultrasonic, nylon 6 monofilament is passed through pyrrole aqueous solution in a certain time to make pyrrole attached to the fiber; 3) adding oxidant to make pyridine. In situ polymerization of the fiber on the polypyrrole conductive layer; 4) water washing, the nylon 6 monofilament fiber surface is re contracted and stable, making polypyrrole firmly fixed on the fiber; finally, the filament collects the filament and dried at room temperature at room temperature to get polyamide conductive fiber. The ultrasonic infiltration method for preparing polyamide conductive fiber can prepare polyamide conductive fiber with conductive layer.
【技术实现步骤摘要】
超声浸润法制备聚酰胺导电纤维的方法
本专利技术涉及一种超声浸润法制备聚酰胺导电纤维的方法，属于化学纤维
技术介绍
聚酰胺俗称尼龙(Nylon)，英文名称Polyamide，它是大分子主链重复单元中含有酰胺基团的高聚物的总称。聚酰胺可由内酸胺开环聚合制得，也可由二元胺与二元酸缩聚等得到的。聚酰胺(PA)是指主链节含有极性酰胺基团(-CO-NH一)的高聚物。最初用作制造纤维的原料，后来由于PA具有强韧、耐磨、自润滑、使用温度范围宽成为目前工业中应用广泛的一种工程塑料。PA广泛用来代替铜及其他等优点，有色金属制作机械、化工、电器零件，如柴油发动机燃油泵齿轮、水泵、高压密封圈、输油管等。是美国DuPont公司最先开发用于纤维的树脂，于1939年实现工业化。20世纪50年代开始开发和生产注塑制品，以取代金属满足下游工业制品轻量化、降低成本的要求。PA具有良好的综合性能，包括力学性能、耐热性、耐磨损性、耐化学药品性和自润滑性，且摩擦系数低，有一定的阻燃性，易于加工，适于用玻璃纤维和其它填料填充增强改性，提高性能和扩大应用范围。PA的品种繁多，有PA6、PA66、PA11、PA12、PA46、PA610、PA612、PAl010等，以及近几年开发的半芳香族尼龙PA6T和特种尼龙等新品种。导电纤维（英文：electroconductivefiber）是20世纪60年代出现的一种新的纤维品种，它一般是指导电率大于10-7Ω-1.cm-1的纤维。这类纤维具有良好的导电性和耐久性，特别是在低湿度下仍具有良好的耐久抗静电性，因此在工业、民用等领域有着很大的用途。现有的导...
【技术保护点】
1.超声浸润法制备聚酰胺导电纤维的方法,其特征在于，包括如下步骤：1）以尼龙6单丝为原料，洗净后晾干；2）在超声波作用下，尼龙6单丝在一定时间内通过吡咯水溶液中，使得吡咯附着在纤维上；3）加入氧化剂，使得吡咯在纤维上原位聚合生成聚吡咯导电层；4）水洗，使尼龙6单丝纤维表层重新收缩、稳定，使得聚吡咯导电层牢牢固定在纤维上；最后经过丝筒收集长丝并在室温下于通风处干燥，得到聚酰胺导电纤维。
【技术特征摘要】
1.超声浸润法制备聚酰胺导电纤维的方法,其特征在于，包括如下步骤：1）以尼龙6单丝为原料，洗净后晾干；2）在超声波作用下，尼龙6单丝在一定时间内通过吡咯水溶液中，使得吡咯附着在纤维上；3）加入...
【专利技术属性】
技术研发人员：顾华来，
申请(专利权)人：江苏华洋尼龙有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。