The present invention provides an aluminum alloy and its surface treatment method and application. The method comprises the following steps: Anodizing an aluminum alloy substrate to form an anodic oxide layer on the outer surface of the aluminum alloy substrate, wherein the anodizing uses a sulphuric acid solution with a concentration equal to or equal to 260g/L, and the voltage of the anodic oxidation is less than equal to 9V. The use of low anode oxidation voltage can effectively solve the problem of surface starting point. The use of high concentration sulphuric acid solution can improve the conductivity of the solution, further improve the gloss of aluminum alloy, reduce the surface roughness, and realize the appearance of bright surface stainless steel.
【技术实现步骤摘要】
铝合金及其表面处理方法和应用
本专利技术涉及铝合金加工和电子设备
，具体的，涉及铝合金及其表面处理方法和应用。
技术介绍
随着技术和人们审美的发展，用户对电子设备的外观要求越来越高，高光不锈钢外观效果得到很多用户的青睐，然而采用不锈钢材质成本高、重量大，不符合轻薄化的发展趋势。铝合金密度较小且质量较轻，但铝合金因为比较软无法直接作外观面,需要阳极氧化保护,但普通阳极氧化出来会存在表面发麻、消光严重等问题，无法达到亮面不锈钢的外观效果。因而，目前关于电子设备外观的相关技术仍有待改进。
技术实现思路
本专利技术旨在至少在一定程度上解决相关技术中的技术问题之一。为此，本专利技术的一个目的在于提出一种操作简单、成本低廉、能够有效实现亮面不锈钢外观效果的铝合金表面处理方法。在本专利技术的一个方面，本专利技术提供了一种铝合金表面处理方法。根据本专利技术的实施例，该方法包括：对铝合金基材进行阳极氧化，以在所述铝合金基材外表面形成阳极氧化层，其中，所述阳极氧化采用浓度大于260g/L的硫酸溶液，所述阳极氧化的电压小于9V。专利技术人发现，通过采用较低的阳极氧化电压可以有效解决表...
【技术保护点】
1.一种铝合金表面处理方法，其特征在于，包括：对铝合金基材进行阳极氧化，以在所述铝合金基材外表面形成阳极氧化层，其中，所述阳极氧化采用浓度大于等于260g/L的硫酸溶液，所述阳极氧化的电压小于等于9V。
【技术特征摘要】
1.一种铝合金表面处理方法，其特征在于，包括：对铝合金基材进行阳极氧化，以在所述铝合金基材外表面形成阳极氧化层，其中，所述阳极氧化采用浓度大于等于260g/L的硫酸溶液，所述阳极氧化的电压小于等于9V。2.根据权利要求1所述的铝合金表面处理方法，其特征在于，所述硫酸溶液的浓度为260g/L～350g/L。3.根据权利要求1所述的铝合金表面处理方法，其特征在于，所述阳极氧化膜的厚度为6～12微米。4.根据权利要求1所述的铝合金表面处理方法，其特征在于，所述阳极氧化还满足以下条件的至少之一：温度为20～24摄氏度，时间为40～60分钟。5.根据权利要求1所述的铝合金表面处理方法，...
【专利技术属性】
技术研发人员：侯体波，
申请(专利权)人：广东欧珀移动通信有限公司，
类型：发明
国别省市：广东,44