一种增加气肥煤配入量的方法技术

本发明专利技术公开了一种增加气肥煤配入量的方法，1）磨制并收集焦粉，焦粉的粒度为0.2mm；2）破碎气肥煤，使得气肥煤的粒度为3mm；3）把所述的焦粉和气肥煤按照1：30的重量比混匀；4）将混匀后的煤料通过高压对辊造粒，使得造粒后的煤料粒度为5mm；5）在原有气肥煤的使用比例上提高3.5个百分点配入造粒后的煤料进行炼焦即可。本发明专利技术能在原有使用气肥煤的基础上，进一步增加其用量，使得疆内炼焦煤资源得到充分利用，降低企业生产成本。

A method to increase the distribution of gas fat coal

The invention discloses a method for increasing the distribution of gas fat coal, 1) grinding and collecting coke powder, the particle size of coke powder is 0.2mm; 2) crushing gas fat coal, making the granularity of gas fat coal 3mm; 3) to mix the coke and gas fat coal according to the 1:30 weight ratio; 4) the mixed coal is granulation through high pressure to the roll, making the coals made by high pressure. The particle size of the coal after granulation is 5 mm; 5) Increase the proportion of the original gas and fertilizer coal by 3.5 percentage points to blend the coal after granulation for coking. The invention can further increase the amount of the gas fat coal on the basis of using the gas fat coal, making the coking coal resources fully utilized and reducing the production cost of the enterprise.

【技术实现步骤摘要】
一种增加气肥煤配入量的方法
本专利技术涉及一种增加气肥煤配入量的方法。
技术介绍
1890煤是八钢独有的优质气肥煤，但其配加量的提高对焦炭热态的影响一直是困扰用量不能提高的致命因素。通过1890极限配入的实验，现已掌握1890配量最高可达40%，但因现实焦煤资源限制，而无法实际生产应用。目前1890的实际产能与实际配煤需求量不对等，自有矿产资源的优势不能充分发挥。世界炼焦煤资源储量与实际需求不相符，一方面是对主焦煤的依靠和需求，另一方面是主焦煤的自然储量远低于气肥煤的实际储量，如何增加气肥煤的炼焦配入量，是所有配煤技术人员共同思考的问题。
技术实现思路
本专利技术的目的在于提供一种增加气肥煤配入量的方法，在原有使用气肥煤的基础上，进一步增加其用量，使得疆内炼焦煤资源得到充分利用。本专利技术的目的是这样实现的：一种增加气肥煤配入量的方法，1）磨制并收集焦粉，焦粉的粒度为0.2mm；2）破碎气肥煤，使得气肥煤的粒度为3mm；3）把所述的焦粉和气肥煤按照1：30的重量比混匀；4）将混匀后的煤料通过高压对辊造粒，使得造粒后的煤料粒度为5mm；5）在原有气肥煤的使用比例上提高3.5个百分点配入造粒本文档来自技高网...

【技术保护点】
1.一种增加气肥煤配入量的方法，其特征在于： 1）磨制并收集焦粉，焦粉的粒度为0.2mm；2）破碎气肥煤，使得气肥煤的粒度为3mm；3）把所述的焦粉和气肥煤按照1：30的重量比混匀；4）将混匀后的煤料通过高压对辊造粒，使得造粒后的煤料粒度为5mm；5）在原有气肥煤的使用比例上提高3.5个百分点配入造粒后的煤料进行炼焦即可。

【技术特征摘要】
1.一种增加气肥煤配入量的方法，其特征在于：1）磨制并收集焦粉，焦粉的粒度为0.2mm；2）破碎气肥煤，使得气肥煤的粒度为3mm；3）把所述的焦粉和气肥煤按照1...