The invention discloses a nano metal powder reinforced silicon carbide / graphite composite ceramic coating, which includes 100 silicon carbide powder, nano metal powder 2~8 portion, ultra-fine graphite powder 2~8 portion, 5~10 portion of adhesive agent and 1~3 portion of dispersant; it also discloses the preparation methods, including the following steps: S1, grinding mixing; S2, wet ball milling; S3 Composite powder; S4, coating preparation. The beneficial effects of the invention are as follows: green environmental protection, simple spraying process, composite ceramic coating obtained with the advantages of high temperature resistance, abrasion resistance and corrosion resistance of ceramic materials, and both strength and toughness of metal materials.
【技术实现步骤摘要】
纳米金属粉末增强的碳化硅/石墨复合陶瓷涂层及其制备方法
本专利技术涉及陶瓷
，特别是纳米金属粉末增强的碳化硅/石墨复合陶瓷涂层及其制备方法。
技术介绍
碳化硅陶瓷涂层，具有耐高温、耐化学腐蚀、导热系数高、热膨胀系数低、介电及透波等优点，已被广泛地应用于宇航、国防、石油、化工、机械、冶金、交通和电力等诸多领域。20世纪90年代以来,碳化硅陶瓷涂层应用得到了持续高速的发展。在欧美发达国家，年增长率持续保持在12％以上,有的领域(如航空发动机碳化硅热障涂层)应用的年增长率高达20％。但是，由于碳化硅属于具有较强共价键结合的稳定化合物，因此很难实现高温烧结环境下的材料致密性，使该材料出现脆性大、易产生裂纹和使用寿命短等缺点，限制了进一步的应用推广。所以，亟需开发具有微纳米微观致密结构的高强度、高韧性、耐高温、耐磨和耐腐蚀的碳化硅复合陶瓷涂层。纳米金属粉末由于本身晶粒的细化，可使晶界数量大幅度增加。被引入陶瓷涂层后，可提高涂层与基体的界面结合强度、断裂韧性、耐蚀耐磨性和抗高温氧化性等。超细石墨粉体材料由于独特的“体积效应”和“表面效应”，使其具有化学活性高、磁性强、热...
【技术保护点】
1.纳米金属粉末增强的碳化硅/石墨复合陶瓷涂层，其特征在于：它包括碳化硅微粉100份、纳米金属粉末2～8份、超细石墨粉末2～8份、粘接剂5～10份和分散剂1～3份。
【技术特征摘要】
1.纳米金属粉末增强的碳化硅/石墨复合陶瓷涂层，其特征在于：它包括碳化硅微粉100份、纳米金属粉末2～8份、超细石墨粉末2～8份、粘接剂5～10份和分散剂1～3份。2.根据权利要求1所述的纳米金属粉末增强的碳化硅/石墨复合陶瓷涂层，其特征在于：所述碳化硅微粉的D50直径为5～10微米，碳化硅微粉的纯度大于99.5％。3.根据权利要求1所述的纳米金属粉末增强的碳化硅/石墨复合陶瓷涂层，其特征在于：所述纳米金属粉末为纳米钨粉、纳米铁粉、纳米铝粉、纳米银粉和纳米锆粉中的任意或多种。4.根据权利要求1所述的纳米金属粉末增强的碳化硅/石墨复合陶瓷涂层，其特征在于：所述超细石墨粉末的D50直径为10～30微米，超细石墨粉末纯度大于99.5％。5.根据权利要求1所述的纳米金属粉末增强的碳化硅/石墨复合陶瓷涂层，其特征在于：所述粘接剂为羧甲基纤维素钠、钾水玻璃、羟乙基纤维素和木质素纤维中的或多种。6.根据权利要求1所...
【专利技术属性】
技术研发人员：楼日新，
申请(专利权)人：四川共拓新材料股份有限公司，
类型：发明
国别省市：四川,51