The invention discloses a narrow lap welding method for 250MPa grade high strength IF steel, which is welded according to the formula, compensation amount, welding speed, welding pressure, welding temperature and welding current. By calculating the method of determining the parameters of welding parameters, this method avoids the defects of manual experience setting of welding parameters and avoids the defect that the welding quality can not be scientifically measured by the on-line measurement of weld heat. The quality of the welding welding is controlled scientifically and reasonably, and the stability of the welding quality is raised. This method can make the narrow lap welding meet the requirement of the production process, avoid the phenomenon of stopping and speed reduction in the continuous annealing process, and ensure the stability of the product quality of the continuous annealing line.
【技术实现步骤摘要】
一种250MPa级高强IF钢的窄搭接焊方法
本专利技术涉及一种焊接工艺，尤其是一种250MPa级高强IF钢的窄搭接焊方法。
技术介绍
250MPa级高强IF钢经酸轧后要在连续退火生产线上完成退火，最终得到成品。在带钢连续退火生产线上，将带钢头、尾焊接起来，实现连续生产，是提高生产效率，降低成本的必要技术手段。焊核是电阻焊时，电流通过上下层金属，在二层金属之间因电阻和上下电极共同作用下发热形成熔化核心，通电结束同时压力延时释放后，核心凝固就形成焊核。与其他特征区相比，焊核的冲击韧性值最低而硬度最高，这主要是由于焊核主要由铸造组织以及晶界相组成。250MPa级高强IF钢对焊接热输入要求非常严格，焊缝热量过大过小都不好，过大易产生过热，过小易产生淬硬组织。焊缝热量是影响焊接质量的关键因素，而连续退火生产线高节奏的生产特点决定了在线无法检测焊缝热量，以往焊接参数只能通过人工经验设定，估测焊核大小，由于经验的不确定性，导致连续退火焊接过程频繁出现降速甚至停车问题，严重影响连续退火生产线的质量稳定性。连续退火生产线的窄搭接焊工艺在现有操作中完全依赖人工经验。窄搭接焊属于电阻焊...
【技术保护点】
1.一种250MPa级高强IF钢的窄搭接焊方法，其特征在于，按下述公式Ⅰ‑Ⅵ计算所得的搭接量、补偿量、焊接速度、焊接压力、焊接温度和焊接电流进行焊接；W＝0.25+0.26*H Ⅰ；C＝0.2+0.1*H Ⅱ；V＝19.35‑2.74*H Ⅲ；P＝1.25+3.34*H Ⅳ；ΔT＝750+95*H Ⅴ；
【技术特征摘要】
1.一种250MPa级高强IF钢的窄搭接焊方法，其特征在于，按下述公式Ⅰ-Ⅵ计算所得的搭接量、补偿量、焊接速度、焊接压力、焊接温度和焊接电流进行焊接；W＝0.25+0.26*HⅠ；C＝0.2+0.1*HⅡ；V＝19.35-2.74*HⅢ；P＝1.25+3.34*HⅣ；ΔT＝750+95*HⅤ；式中：W是搭接量，单位为mm；H是焊接厚度，单位为mm；C是补偿量，单位为mm；V是焊接速度，单位为m/min；P是焊接压力，单位为KN；ΔT是焊接温度，单位为℃；I是焊接电流，单位为A；K、α、β、ε为常数，K/ε取值0.247、α取值-2.75、β取值为0.75；ρ...
【专利技术属性】
技术研发人员：何方，刘自权，李佩，吕超杰，白瑞召，姜丽梅，王风强，
申请(专利权)人：邯郸钢铁集团有限责任公司，河钢股份有限公司邯郸分公司，