The invention is a dry cello formula and a manufacturing method thereof. Alkyd polymer (solid content 80%) 30 kg, styrene 15 kilogram, polyethylene glycol (600) 0.01 kg, two butyltin two laurate 1 kg, polyamide wax (n-butanol, petroleum brain mixture) 2 kg, ortho benzene unsaturated polyester resin 50 kilogram, polyvinyl alcohol butyral 10.1 kilogram, ethyl acetate 10 kilogram, 2, 2 dihydroxymethylbutyric acid 0.1 kg. The alkyd resin polymer (solid content 80%), styrene, polyethylene glycol (600), two butyl tin two laurel ester and polyamide wax (n-butanol and petroleum brain mixture) were mixed for 30 minutes for 30 minutes. After that, the phthalic unsaturated polyester resin, polyvinyl alcohol butanal, ethyl acetate and 2,2 dihydroxymethylbutyric acid were added. Keep stirring for 30 minutes.
【技术实现步骤摘要】
一种易干的大提琴漆配方及其制造方法
本专利技术涉及化工涂料制造领域,具体说是一种改良大提琴漆漆膜干燥速率的配方及其制造方法。
技术介绍
现在市场上的大提琴漆普遍存在黏度大、漆膜干燥效果不理想的问题,喷涂后需要静置很长时间干燥,影响了大提琴漆的施工时间。同时,在长时间的干燥过程中,也容易受外界环境的影响,破坏大提琴的美观。
技术实现思路
本专利技术解决现有的大提琴漆漆膜干燥慢的问题,专利技术一种提高漆膜干燥速率的配方及其制造方法。本专利技术的技术方案是,一种解决大提琴漆漆膜干燥速率慢的配方及其制造方法,包括:醇酸树脂聚合体(固含量80%)、苯乙烯、聚乙二醇(600)、二丁基锡二月桂酸酯、聚酰胺蜡(正丁醇、石油脑混合物)、邻苯型不饱和聚酯树脂、聚乙烯醇缩丁醛、乙酸乙酯、2,2-二羟甲基丁酸。组分重量比:醇酸树脂聚合体(固含量80%)25~35%、苯乙烯10~20%、聚乙二醇(600)0.01~0.1%、二丁基锡二月桂酸酯0.1~2%、聚酰胺蜡(正丁醇、石油脑混合物)1~5%、邻苯型不饱和聚酯树脂40~50%、聚乙烯醇缩丁醛0.01~0.1%、乙酸乙酯5~15%、2,2-二羟甲基丁酸0.1~1.0%。制造方法:将醇酸树脂聚合体(固含量80%)、苯乙烯、聚乙二醇(600)、二丁基锡二月桂酸酯和聚酰胺蜡(正丁醇、石油脑混合物)混合,持续搅拌30分钟,之后加入邻苯型不饱和聚酯树脂、聚乙烯醇缩丁醛、乙酸乙酯、2,2-二羟甲基丁酸,继续搅拌30分钟即可。醇酸树脂聚合体(固含量80%)、苯乙烯和邻苯型不饱和聚酯树脂是主要的成膜物质,其中苯乙烯也是溶剂,同时也参与反应,在引发剂的 ...
【技术保护点】
1.本专利技术解决现有的大提琴漆漆膜干燥慢的问题,专利技术一种提高漆膜干燥速率的配方及其制造方法。
【技术特征摘要】
1.本发明解决现有的大提琴漆漆膜干燥慢的问题,发明一种提高漆膜干燥速率的配方及其制造方法。2.本发明的技术方案是,一种解决大提琴漆漆膜干燥速率慢的配方及其制造方法,包括:醇酸树...