The present invention is an anticorrosion and cold resistant coating, which consists of the following weight parts: ABS resin 15, 29 copies, 5 polyurethane resins, 11 polyvinyl chloride 21 copies, 6 carbon black 6 10 copies, 9 bentonite, 9 copies of calcium carbonate, 8 calcium carbonate, talcum powder Titanium 2 is 7, carboxymethyl cellulose 5 8 copies. The coating made by the invention has good anticorrosion performance. The coating has good adhesion, toughness, wear resistance, acid and alkaline resistance, and has good cold resistance and low price. It can keep good performance in low temperature environment, and it is not easy to crack at low temperature.
【技术实现步骤摘要】
一种防腐耐寒涂料
本专利技术涉及一种涂料,具体的说是涉及一种防腐耐寒涂料。
技术介绍
随着经济的发展和社会的进步,人们对涂料的性能要求也越来越高,尤其是在气候寒冷的北方地区,涂料在低温的环境下很容易出现开裂、耐碱腐蚀性能也会变差,耐寒性能差。
技术实现思路
为了解决上述问题,本专利技术提供了一种耐寒涂料,并且具有良好的耐腐蚀能力。为了达到上述目的,本专利技术是通过以下技术方案实现的:本专利技术是一种防腐耐寒涂料,所述涂料包括如下重量份的原料:ABS树脂15-29份,聚氨酯树脂5-16份,聚氯乙烯树脂11-21份,炭黑6-10份,膨润土5-9份,轻质碳酸钙8-16份,邻苯二甲酸二辛酯5-13份,滑石粉6-16份,纳米二氧化钛2-7份,羧甲基纤维素5-8份。优选的:涂料包括如下重量份的原料:ABS树脂29份,聚氨酯树脂5份,聚氯乙烯树脂11份,炭黑6份,膨润土5份,轻质碳酸钙8份,邻苯二甲酸二辛酯5份,滑石粉6份,纳米二氧化钛2份,羧甲基纤维素5份。优选的:涂料包括如下重量份的原料:ABS树脂15份,聚氨酯树脂16份,聚氯乙烯树脂21份,炭黑10份,膨润土9份,轻质碳酸钙16份,邻苯二甲酸二辛酯13份,滑石粉16份,纳米二氧化钛7份,羧甲基纤维素8份。优选的:涂料包括如下重量份的原料:ABS树脂22份,聚氨酯树脂11份,聚氯乙烯树脂17份,炭黑8份,膨润土7份,轻质碳酸钙12份,邻苯二甲酸二辛酯9份,滑石粉11份,纳米二氧化钛5份,羧甲基纤维素5份。本专利技术的有益效果是:ABS树脂具有质轻、耐寒、抗冲击性能较好等优点,使得本涂料具有良好的耐寒、耐冲击性能,邻苯二 ...
【技术保护点】
1.一种防腐耐寒涂料,其特征在于:所述涂料包括如下重量份的原料:ABS树脂15‑29份,聚氨酯树脂5‑16份,聚氯乙烯树脂11‑21份,炭黑6‑10份,膨润土5‑9份,轻质碳酸钙8‑16份,邻苯二甲酸二辛酯5‑13份,滑石粉6‑16份,纳米二氧化钛2‑7份,羧甲基纤维素5‑8份。
【技术特征摘要】
1.一种防腐耐寒涂料,其特征在于:所述涂料包括如下重量份的原料:ABS树脂15-29份,聚氨酯树脂5-16份,聚氯乙烯树脂11-21份,炭黑6-10份,膨润土5-9份,轻质碳酸钙8-16份,邻苯二甲酸二辛酯5-13份,滑石粉6-16份,纳米二氧化钛2-7份,羧甲基纤维素5-8份。2.根据权利要求1所述一种防腐耐寒涂料,其特征在于:所述涂料包括如下重量份的原料:ABS树脂29份,聚氨酯树脂5份,聚氯乙烯树脂11份,炭黑6份,膨润土5份,轻质碳酸钙8份,邻苯二甲酸二辛酯5份,滑石粉6份,纳米二氧化钛2份,羧甲基纤...
【专利技术属性】
技术研发人员:黄新良,
申请(专利权)人:丹阳市海信涂料化工厂,
类型:发明
国别省市:江苏,32