The invention provides a high strength and toughness magnesium alloy and a preparation method thereof. A high strength and tough magnesium alloy contains the following components: Y 3.5 ~ 10%, Sm 2 ~ 5%, Zn 0.2 ~ 2%, Zr 0.3 ~ 0.8%, and the rest Mg and unavoidable impurities according to the weight percentage. The invention adopts Sm and Y as the main alloy element with lower price, and adds a proper amount of Zn to regulate the type and quantity of the precipitated phase in the matrix. The content of the rare earth element is lower than that of the other high rare-earth content magnesium alloys. Therefore, the cost is lower, and the high strength and toughness are both high, and it has a good prospect of industrial application.
【技术实现步骤摘要】
一种高强韧镁合金及其制备方法
本专利技术涉及镁合金
，尤其是涉及一种高强韧镁合金及其制备方法。
技术介绍
镁合金具有比强度和比弹性模量高、阻尼吸震降噪性能优越、铸造成型性好、易于回收利用等一系列优点，已受到越来越多的关注。但是，由于镁合金绝对强度低，且其室温成形性差，还难以大量生产并应用于承载结构件，从而限制了进一步的应用。目前高强韧稀土镁合金主要包含Gd、Y、Ho、Er或者同时包含多种价格昂贵的稀土元素，其强化原理是这些稀土在镁基体中具有较高的固溶度，低温时效过程中能够析出纳米相，从而强化合金。为了实现良好的强化效果，需要加入高含量的稀土，导致合金成本较高。如专利申请200610119266.3公开了“高强度耐热镁合金及其制备方法”，该镁合金的质量成分为3.0％～12.0％Gd、2.0％～6.0％Sm、0.35％～0.8％Zr，余量为Mg；该合金铸造态经均匀化和时效处理后得到其室温拉伸性能最高达到抗拉强度为370MPa，延伸率为5.2％。虽然该合金具有高强韧性，但由于Gd是一种价格较贵的稀土元素，限制了该合金的工业化应用。因此，开发低成本高强韧镁合金对拓宽...
【技术保护点】
1.一种高强韧镁合金，其特征在于，包含以下成分：按重量百分比计，Y 3.5～10.0％，Sm 2.0～5.0％，Zn 0.2～2％，Zr 0.3～0.8％，其余为Mg和不可避免的杂质。
【技术特征摘要】
1.一种高强韧镁合金，其特征在于，包含以下成分：按重量百分比计，Y3.5～10.0％，Sm2.0～5.0％，Zn0.2～2％，Zr0.3～0.8％，其余为Mg和不可避免的杂质。2.根据权利要求1所述的高强韧镁合金，其特征在于，按重量百分比计，Y含量为4～10％，优选5～10％，优选5～7％，优选5～6％或7～10％。3.根据权利要求1所述的高强韧镁合金，其特征在于，按重量百分比计，Sm含量为3～5％，优选3.5～5％，优选4～5％或3～4％。4.根据权利要求1所述的高强韧镁合金，其特征在于，按重量百分比计，Zn含量为0.5～2％，优选0.8～2％，优选1～2％或0.1％。5.根据权利要求1所述的高强韧镁合金，其特征在于，按重量百分比计，Zr含量为0.5～0.8％，或0.3～0.5％。6.根据权利要求1所述的高强韧镁合金，其特征在于，Y和Sm的总含量在13.5wt％以下，优选13wt％以下，优选12wt％以下，优选9.5wt％以下，优选8wt％以下，优选6～13.5wt％，优选8～13.5wt％，优选9.5～13.5wt％，优选12～13.5wt％，优选6～12wt％。7.根据权利要求1-6任一项所述的高强韧镁合金，其特征在于，按重量百分...
【专利技术属性】
技术研发人员：肖文龙，吕绍元，马朝利，王方，黄菲菲，奚家冰，
申请(专利权)人：北京航空航天大学，
类型：发明
国别省市：北京,11