一种防腐蚀阻燃复合电缆护套料制造技术

本发明专利技术涉及电缆领域，具体涉及一种防腐蚀阻燃复合电缆护套料。该种电缆外护套料，由以下按照重量份数的原料组成：聚苯氧基树脂55‑75份、顺丁橡胶20‑26份、聚四氟乙烯10‑25份、稳定剂2‑8份、二异丙苯7‑10份、醋酸乙烯酯共聚物4‑9份、抗氧剂1‑5份、水合硼酸锌3‑8份、紫外线吸收剂7‑11份、抗老化剂1‑4份和增强填料3‑7份。本发明专利技术配方科学，生产成本低，增强了电缆的阻燃性能、耐酸碱腐蚀性能、抗冲击性能，同时改善了电缆的可拉伸强度，绝缘性能良好。

Anticorrosion and flame retardant composite cable sheath

The invention relates to the cable field, in particular to an anticorrosive flame retardant composite cable sheathing material. The outer sheath of the cable consists of the following ingredients: polyphenoxy resin 55, 75, 20, 26, 10, 25, 2, two, two, 7, 10, vinyl acetate copolymers 4, antioxidants, zinc borate, and UV absorbers 7, 11, 1, 4, and 3, 7, respectively. The invention has a low production cost, enhances the flame retardancy, acid alkali corrosion resistance and impact resistance of the cable, and improves the tensile strength of the cable and the insulation performance is good.

【技术实现步骤摘要】
一种防腐蚀阻燃复合电缆护套料
本专利技术涉及电缆领域，具体涉及一种防腐蚀阻燃复合电缆护套料。
技术介绍
目前，随着社会经济的发展，电线电缆用量迅速增长，对电缆的质量要求也不断的提高，比如在钢铁、冶金、电力、化工、石油等行业内使用的电缆，对电缆的阻燃性、抗酸碱腐蚀性、使用寿命、抗紫外线防辐射性能、抗牵拉性、防水、抗弯折以及耐高温方面的要求都特别高，只有符合要求，才能提高这些领域内生产制造时的安全性。
技术实现思路
为了解决上述背景中提到的问题，本专利技术目的在于提供一种防腐蚀阻燃复合电缆护套料。为实现上述目的，本专利技术提供如下技术方案：一种防腐蚀阻燃复合电缆护套料，由以下按照重量份数的原料组成：氯丁橡胶50-70份、聚烯烃树脂30-45份、钛白粉10-15份、二异丙苯5-10份、硅酸铝4-10份、滑石粉5-7份、聚磷酸铵10-15份、硬脂酸钙3-8份、改性煅烧陶土5-12份、羟基硅油1-3份、阻燃剂1-5份、和增强填料3-7份。进一步，上述防腐蚀阻燃复合电缆护套料，由以下按照重量份数的原料组成：氯丁橡胶60-70份、聚烯烃树脂38-45份、钛白粉13-15份、二异丙苯7-10份、硅酸铝7本文档来自技高网...

【技术保护点】
1.一种防腐蚀阻燃复合电缆护套料，其特征在于，由以下按照重量份数的原料组成：氯丁橡胶50‑70份、聚烯烃树脂30‑45份、钛白粉10‑15份、二异丙苯5‑10份、硅酸铝4‑10份、滑石粉5‑7份、聚磷酸铵10‑15份、硬脂酸钙3‑8份、改性煅烧陶土5‑12份、羟基硅油1‑3份、阻燃剂1‑5份、和增强填料3‑7份。

【技术特征摘要】
1.一种防腐蚀阻燃复合电缆护套料，其特征在于，由以下按照重量份数的原料组成：氯丁橡胶50-70份、聚烯烃树脂30-45份、钛白粉10-15份、二异丙苯5-10份、硅酸铝4-10份、滑石粉5-7份、聚磷酸铵10-15份、硬脂酸钙3-8份、改性煅烧陶土5-12份、羟基硅油1-3份、阻燃剂1-5份、和增强填料3-7份。2.根据权利要求1所述的防腐蚀阻燃复合电缆护套料，其特征在于，由以下按照重量份数的原料组成：氯丁橡胶60-70份、聚烯烃树脂38-45份、钛白粉...

【专利技术属性】
技术研发人员：徐孝立，郑志刚，
申请(专利权)人：淮北市天相电缆有限责任公司，
类型：发明
国别省市：安徽,34