The invention discloses a method for preparing silver nanotube with copper nanowires as a template. The method uses copper nanowires as a template and silver nitrate is used as silver source to electroless silver plating. After annealing, the copper nanowires are removed by etching solution and silver nanotubes can be prepared. The method uses the copper nanowires as the template, the silver nitrate as the silver source of the plating bath, the process of making the nanotubes through the annealing and etching solution washing and removing the template. The whole process has less energy consumption, and it is easy to operate and is suitable for large-scale production.
【技术实现步骤摘要】
一种以铜纳米线为模板制备银纳米管的方法
本专利技术属于材料化学领域，涉及一种纳米材料制备与应用传感技术，具体为一种以铜纳米线为模板制备银纳米管的方法。
技术介绍
纳米材料在尺寸和结构上的特异性，使得纳米材料具有很多不同于常规材料的特殊性质，比如较高的晶体缺陷密度、界面所占体积百分数很大、极细的晶粒尺寸等，这些结构上独特性质使得纳米材料的电学、光学、热学、力学、磁学等性能，无论在宏观或微观方面都与常规大块材料大不相同。在众多的纳米材料中，管状纳米结构材料如银纳米管因其独特的物理、化学性能在光、电、催化和存储等领域表现出重要的应用价值。如果对其内壁、外壁或者端口进行修饰，会进一步表现出独特的性能。现有的银纳米管制备方法存在步骤繁琐、制备成本高、对设备要求高等弊端，因此，如何低成本的大规模制备银纳米管成为一项具有重大意义的课题。
技术实现思路
解决的技术问题：为了克服现有技术的缺陷，获得一种操作简便、能耗少、适合大规模制备管状纳米结构材料，本专利技术提供了一种以铜纳米线为模板制备银纳米管的方法。技术方案：一种以铜纳米线为模板制备银纳米管的方法，所述方法以铜纳米线为模板，以硝...
【技术保护点】
1.一种以铜纳米线为模板制备银纳米管的方法，其特征在于，所述方法以铜纳米线为模板，以硝酸银为银源进行化学镀银，退火过程后采用蚀刻液去除铜纳米线，即可制得银纳米管。
【技术特征摘要】
1.一种以铜纳米线为模板制备银纳米管的方法，其特征在于，所述方法以铜纳米线为模板，以硝酸银为银源进行化学镀银，退火过程后采用蚀刻液去除铜纳米线，即可制得银纳米管。2.根据权利要求1所述的一种以铜纳米线为模板制备银纳米管的方法，其特征在于，所述方法具体包括以下步骤：(1)将铜纳米线原料分散至镀液中，所述镀液中硝酸银和三乙烯四胺的摩尔比例为1:1～1:2，0～60℃水浴条件下搅拌反应10～60min；(2)将步骤(1)得到的铜金异质结构100～300℃条件下退火处理1～10h；(3)将退火处理后的样品分散至蚀刻液中反应6～24小时制得，所述蚀刻液为含有二价铜...
【专利技术属性】
技术研发人员：张广维，吴雪卫，陈剑宇，孙志鹏，李谊，马延文，仪明东，黄艳琴，罗孟成，
申请(专利权)人：南京邮电大学，
类型：发明
国别省市：江苏,32