The invention belongs to the field of environmental protection materials, in particular to a manufacturing method of different color biomass decorative bricks. The method uses poplar wood fiber, corn straw, calcium hydroxide and water color slurry as raw materials to suppress different color biomass decorative bricks, in which the calcium hydroxide and water color color pulp are prepared as water based calcium hydroxide color pulp. And then mixed with poplar and corn straw to prepare different color biomass decorative bricks. The different color biomass decoration bricks have accurate saturation and lightness color, filling the blank in this field.
【技术实现步骤摘要】
一种不同颜色生物质装饰砖的制造方法
本专利技术属于环保材料领域,具体涉及一种不同颜色生物质装饰砖的制造方法。
技术介绍
我国杨树总面积已达1010多万hm2,木材蓄积量达5.49亿m3。我国年产秸秆7亿吨,小麦秸秆和稻草年产量约为4亿吨,玉米秸秆的年产量约为2.5亿吨,秸秆资源丰富。小麦、玉米秸秆在田间直接焚烧不仅浪费资源,而且还严重污染环境,产生“雾霾”,因此,加强秸秆的综合开发利用是发展现代化农业的必然趋势。目前,杨木主要用来制造胶合板、纤维板和刨花板,加工途径单一,附加值低,利润率为7.5%。小麦、玉米秸秆的利用包括还田、饲料转化、能源化及工业材料应用等领域,捆扎的小麦、玉米秸秆草砖作为保温墙体使用。石灰浆是人类使用最早的无机胶凝材料,属于气硬性胶凝材料,能与CO2发生碳化反应,生成CaCO3。Ca(OH)2饱和溶液的PH值在12.4左右,能溶蚀细菌的细胞膜,具有杀菌作用。Ca(OH)2作为阻燃剂,不产生有毒、有腐蚀的气体,抑烟。同时,它是优良的粘结材料,廉价且来源丰富,常用于建筑领域。具有不同程度的色彩的装饰砖可用于不同的场所。如民用建筑或公共建筑,既可以 ...
【技术保护点】
1.一种不同颜色生物质装饰砖的制造方法,其特征在于:具体步骤为:水性氢氧化钙色浆的配置:称量规定质量的氢氧化钙,按比例混合水性色浆,搅拌均匀成水性氢氧化钙色浆;水性氢氧化钙色浆的干燥:水性氢氧化钙色浆放置在规定的干燥条件下干燥;混合料搅拌:干燥后的水性氢氧化钙色浆,与杨木纤维和玉米秸秆纤维,搅拌均匀;不同颜色生物质装饰砖模压:水性氢氧化钙色浆、杨木纤维、玉米秸秆纤维混合料,装入模具后,在冷压上模压成型;不同颜色生物质装饰砖干燥:不同颜色生物质装饰砖放在干燥温度60℃、相对湿度30.1%、风速0.20m/s的热空气干燥房干燥48h;不同颜色生物质装饰砖着色效果:干燥后的不同颜 ...
【技术特征摘要】
1.一种不同颜色生物质装饰砖的制造方法,其特征在于:具体步骤为:水性氢氧化钙色浆的配置:称量规定质量的氢氧化钙,按比例混合水性色浆,搅拌均匀成水性氢氧化钙色浆;水性氢氧化钙色浆的干燥:水性氢氧化钙色浆放置在规定的干燥条件下干燥;混合料搅拌:干燥后的水性氢氧化钙色浆,与杨木纤维和玉米秸秆纤维,搅拌均匀;不同颜色生物质装饰砖模压:水性氢氧化钙色浆、杨木纤维、玉米秸秆纤维混合料,装入模具后,在冷压上模压成型;不同颜色生物质装饰砖干燥:不同颜色生物质装饰砖放在干燥温度6...
【专利技术属性】
技术研发人员:路则光,高玉发,王萌,贾万达,马超,董荣丹,
申请(专利权)人:山东农业大学,
类型:发明
国别省市:山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。