本发明专利技术公开了高强度耐腐蚀冷室压铸用含Mo锌合金及其加工工艺。按照重量百分比，该合金的成分为：Ba:0.5‑0.9wt.%,Sc:0.4‑0.6wt.%；Mo:0.8‑1.2wt.%,Si:2.0‑3.5wt.%，In:1.0‑1.5wt.%,Sb:0.2‑0.8wt.%,余量为锌。该锌钡合金具有优异的冷室压铸性能和力学性能，可以用于生产长的薄壁零件。大大提高了生产效率和降低能源消耗。此外，该产品还具有优异的耐腐蚀性能，在电器制造工业和无线电工业中有广泛的用途。

Mo zinc alloy for high strength corrosion resistant cold chamber die casting

The invention discloses a high strength corrosion resistant cold chamber die casting Mo zinc alloy and its processing technology. According to the weight percentage, the composition of the alloy is: Ba:0.5 0.9wt.%, Sc:0.4 0.6wt.%, Mo:0.8 1.2wt.%, Si:2.0 3.5wt.%, In:1.0 1.5wt.%, Sb:0.2 0.8wt.%, and the residue is zinc. The zinc barium alloy has excellent cold chamber die casting properties and mechanical properties, and can be used to produce long thin wall parts. The production efficiency and energy consumption have been greatly improved. In addition, the product has excellent corrosion resistance and is widely used in the electrical manufacturing industry and the radio industry.

【技术实现步骤摘要】
高强度耐腐蚀冷室压铸用含Mo锌合金
本专利技术涉及合金
，具体地说，涉及一种锌钡合金。
技术介绍
锌及锌合金因具有较高的强度、良好的导电导热性以及优良的耐磨耐蚀性，在交通、电力电子、机械、国防军工等行业得到广泛应用。锌中加入锡、铝、铅、锰、硅等元素，可以在保持其力学性能和工艺性能基本不变的前提下，显著提高合金的耐磨性和抗腐蚀性。锌合金可以用于制造汽车及其它工业部门中的气缸活塞销衬套、副连杆衬套、轴承及轴承内衬、圆盘和垫圈等承受摩擦零件;也大量用作轴套、衬套、摇臂、轴承等高强度、高耐磨结构零件;此外，锌合金广泛用作电气设备中的导电、耐热、耐磨零件。近年来，随着我国电力、交通、通讯等行业的快速发展，高性能锌合金材料在各种轨道交通弓网系统、电磁轨道炮电枢/导轨系统、微电子及电器控制插接件等领域得到大量应用。随着材料服役条件向高速、重载、交变温度、腐蚀性介质等苛刻化方向发展，由此导致的磨损、疲劳、断裂等已成为高性能锌合金损伤的主要形式。同时，为满足实际工况使用要求，对锌合金材料的使用性能评价向高品质长寿命等综合性能良好的全方位演变。锌合金按制造加工工艺可分为铸造锌合金和变形锌合金两种类本文档来自技高网...

【技术保护点】
1.一种高强度耐腐蚀冷室压铸用含Mo锌合金；按照重量百分比，该合金的成分为：Ba: 0.5‑0.9wt.%,Sc:0.4‑0.6wt.%；Mo:0.8‑1.2wt.%,Si:2.0‑3.5wt.%，In:1.0‑1.5wt.%, Sb:0.2‑0.8wt.%,余量为锌。

【技术特征摘要】
1.一种高强度耐腐蚀冷室压铸用含Mo锌合金；按照重量百分比，该合金的成分为：Ba:0.5-0.9wt.%,Sc:0.4-0.6wt.%；Mo:0.8-1.2wt.%,Si:2.0-3.5wt.%，In:1.0-1.5wt.%,Sb:0.2-0.8wt.%,余量为锌。2.根据权利要求1所述高强度耐腐蚀冷室压铸用含Mo锌合金，其特征在于包括如下步骤：将如上配比的原料加入到大气保护的感应电炉内，并采用碳化硅坩埚；感应加热到450-500度形成...