The present invention provides a special black masterbatch for water supply polyethylene pipe, including 30~50 parts of low density polyethylene, 38 + 2 copies of carbon black, 5~15 talcum powder, 4~10 antimicrobial agents for water treatment, 0.5 to 5 antioxidants, 0.5 dispersant 0.5, 3 anti aging stabilizer and 8 parts. The preparation method of the black masterbatch includes the following steps: adding each component into a grinding machine, grinding and dispersing and mixing 1 ~ 2H out of the mixture to get the mixture; the mixture is mixed with a twin screw extruder for granulation. The special black masterbatch of water supply polyethylene pipe has good antioxidation and antibacterial property, simple production process, easy operation, easy control and easy to mass production.
【技术实现步骤摘要】
一种给水聚乙烯管道专用黑色母粒及其制备方法
本专利技术涉及一种给水聚乙烯管道专用黑色母粒及其制备方法，属于给水聚乙烯管道高分子材料
技术介绍
黑色母是色母粒的一种，而色母粒是塑料制品中必用的着色剂，其基本组成包含三方面：颜料、载体、添加剂；其中颜料通过载体(通常为热塑性树脂)借助于添加剂分散于目标材料中，其中添加剂可以是分散剂，也可以是具体用途的其它助剂。因为以色母粒为着色剂它具有很多优点，可以使颜料在制品中具有更好的分散性、有利于保持颜料的化学稳定性、保证制品颜色的稳定性、保护操作人员的健康、保护环境的洁净、使用方便等等。国内的给水聚乙烯管道专用黑色母比较简单，一方面和给水聚乙烯管道这种粗放型工程项目本身的特点有关，另一个方面和给水后的水质再处理有关。目前国内给水聚乙烯管道专用黑色母粒主要成分为炭黑+聚乙烯+无机填料碳酸钙，组分结构比较简单，其中无机填料碳酸钙的使用量有的甚至很大，影响了给水聚乙烯管道的颜色均一性、耐压性能、水质的环保等。现有的资源倾向对于市政工程这种粗放型工程投入的精细性改进还不足。现有设备、工艺、专利技术更多的投入到出水端水质的改善...
【技术保护点】
1.一种给水聚乙烯管道专用黑色母粒，其原料按重量份包括如下组分：
【技术特征摘要】
1.一种给水聚乙烯管道专用黑色母粒，其原料按重量份包括如下组分：2.根据权利要求1所述的给水聚乙烯管道专用黑色母粒，其特征在于：所述低密度聚乙烯的数均分子量为20000～50000。3.根据权利要求1所述的给水聚乙烯管道专用黑色母粒，其特征在于：所述滑石粉细度为800目，白度≥90；滑石粉中的氧化镁的质量占比≥28％，二氧化硅的质量占比≥56％。4.根据权利要求1所述的给水聚乙烯管道专用黑色母粒，其特征在于：所述水处理抗菌剂为北京艾斯尔科技有限公司的MK-T-112银锌抗菌剂或者SR-T-801银系抗菌剂。5.根据权利要求1所述的给水聚乙烯管道专用黑色母粒，其特征在于：所述分散剂为十二烷基硫酸钠、乙撑双硬脂酸酰胺或亚甲基双萘磺酸钠中的一种或多种。6.根据权利要求1所述的给水聚乙烯管道专用黑色母粒，其特征在于：所述抗氧化剂为抗氧剂168、抗氧剂1010、抗氧剂B215或抗氧剂1056中的一种或多种。7.根据权利要求1所述的给水聚乙烯管道专用黑色...
【专利技术属性】
技术研发人员：欧阳贵，杨少辉，李楠，肖传富，毕宏江，
申请(专利权)人：上海邦中高分子材料有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。