The invention discloses a contraceptive ring and its preparation method. A contraceptive ring is prepared by silica gel, nano copper powder and crosslinking agent. The silica gel is mixed in a refiner according to the ratio of raw material, and the nano copper powder is gradually added to the silica gel to be mixed uniformly; the crosslinking agent is added to the refiner to form a mixed colloid. The mixed colloid is put into the mould, heated and pressed to make the finished product and then aged, sterilized and sterilized according to the medical and hygienic requirements. The contraceptive ring has smooth surface, soft and elastic texture, no irritation with the human body, and the contact with the human body can not be combined with the human body, and it will not cause bleeding and pain.
【技术实现步骤摘要】
一种节育环及其制备方法
本专利技术涉及医疗领域,具体是一种节育环及其制备方法。
技术介绍
市场原有产品是由硅胶制成结育环后,再将铜环或铜丝缠绕或包裹在制成好的硅胶结育环的表面上,从下而现避孕效果。但不光滑,柔软度不好,弹性度不好,与人体接触有刺激性,与人体接触会与人体结合到一起,会导致出血、疼痛等缺点。还有的结育环里加的药物,加了药物的结育环,等到药物挥发完后就没有了避孕效果,使用寿命太短,不光滑,柔软度不好,弹性度不好,与人体接触有刺激性,与人体接触会与人体结合到一起,会导致出血、疼痛等缺点。
技术实现思路
本专利技术的目的在于提供一种节育环及其制备方法,以解决上述
技术介绍
中提出的问题。为实现上述目的,本专利技术提供如下技术方案:一种节育环,由以下质量份的原料制备而成:硅胶70~80份,纳米铜粉20~30份,交联剂2~3份。一种节育环的制备方法,具体制备步骤如下:1)按上述原料配比取硅胶放入炼胶机内进行混炼;2)按上述原料配比取纳米铜粉逐步地加入到硅胶中进行混合均匀;3)按上述原料配比取交联剂加入到炼胶机中,形成混合胶体;4)将上述混合胶体放入模具,加温压制,模具加温的温度为160~180度,加温压制时间为5~10分钟,制成成品后再依据医疗卫生要求进行老化、灭菌,消毒处理。与现有技术相比,本专利技术的有益效果是:本专利技术节育环表面光滑,质地柔软有弹性,与人体接触无刺激性,与人体接触不会与人体结合到一起,不会导致出血、疼痛。具体实施方式下面将结合本专利技术实施例,对本专利技术实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本专利技术一部分实 ...
【技术保护点】
一种节育环,其特征在于,所述节育环由以下质量份的原料制备而成:硅胶70~80份,纳米铜粉20~30份,交联剂2~3份。
【技术特征摘要】
1.一种节育环,其特征在于,所述节育环由以下质量份的原料制备而成:硅胶70~80份,纳米铜粉20~30份,交联剂2~3份。2.根据权利要求1所述的一种节育环的制备方法,其特征在于,所述节育环的制备方法具体步骤如下:1)按上述原料配比取硅胶放入炼胶机内进行混炼;2)...