The preparation method of Polyaniline / salicylaldehyde modified chitosan inhibitor is to dissolve a certain amount of chitosan in acetic acid solution. Then, a certain amount of salicylaldehyde ethanol solution is added to it. Under the condition of heating and stirring, the chitosan modified by salicylaldehyde can be reacted for a certain time, and then a certain amount of aniline is added to them in turn. After mixing the solution with a certain amount of sulfonic acid, a certain amount of acetic acid solution of ammonium persulfate is added into the mixture. After the reaction, the corrosion inhibitor of Polyaniline / salicylaldehyde modified chitosan can be obtained by filtering, washing and drying the filter cake.
【技术实现步骤摘要】
聚苯胺/水杨醛改性壳聚糖缓蚀剂的制备方法
本专利技术属于金属腐蚀与防护领域，具体涉及缓蚀剂的制备技术，即聚苯胺/水杨醛改性壳聚糖缓蚀剂的制备技术。
技术介绍
目前，添加缓蚀剂是一种行之有效，经济效益显著的防腐手段。早期常用的无机缓蚀剂均能在金属表面形成一层难溶解的保护膜进而阻碍腐蚀介质对金属的破坏。但无机缓蚀剂最大的缺点就是对环境和人体的危害较大以及工作所需浓度较大，早期常用的有机缓蚀剂主要为有机磷化合物，在实际应用中对金属保护不佳的同时还造成富营养化等环境问题，因此寻找绿色天然有机缓蚀剂已成为腐蚀科学的研究热点。壳聚糖是一种天然高分子化合物，其结构中包含杂原子(N和O)，所提供的孤对电子对金属具有较强的吸附力，但由于其分子量较大，从而使得其在水中的溶解性较差。
技术实现思路
本专利技术是聚苯胺/水杨醛改性壳聚糖缓蚀剂的制备方法，其步骤为：（1）室温下，首先将壳聚糖加入到0.35mol/L乙酸溶液，使得壳聚糖与乙酸溶液的质量比为1:120~250，搅拌下，将壳聚糖在乙酸溶液中溶解1~4h；然后，向该壳聚糖的乙酸溶液中加入含有水杨醛的乙醇溶液，使壳聚糖与水杨醛的质量比为...
【技术保护点】
聚苯胺/水杨醛改性壳聚糖缓蚀剂的制备方法，其特征在于，其步骤为：（1）室温下，首先将壳聚糖加入到0.35mol/L乙酸溶液，使得壳聚糖与乙酸溶液的质量比为1:120~250，搅拌下，将壳聚糖在乙酸溶液中溶解1~4h；然后，向该壳聚糖的乙酸溶液中加入含有水杨醛的乙醇溶液，使壳聚糖与水杨醛的质量比为1:4~8，控制加入速度，0.5~1h内加完，然后，加热至30~80ºC，反应4~8h，得水杨醛改性壳聚糖；（2）然后，在5℃下，向上述反应体系中依次加入苯胺、氨基磺酸，使壳聚糖与苯胺的质量比为1:5~10，使苯胺与氨基磺酸的摩尔比为1:1~5，再加入含有过硫酸铵的乙酸溶液做为引发剂...
【技术特征摘要】
1.聚苯胺/水杨醛改性壳聚糖缓蚀剂的制备方法，其特征在于，其步骤为：（1）室温下，首先将壳聚糖加入到0.35mol/L乙酸溶液，使得壳聚糖与乙酸溶液的质量比为1:120~250，搅拌下，将壳聚糖在乙酸溶液中溶解1~4h；然后，向该壳聚糖的乙酸溶液中加入含有水杨醛的乙醇溶液，使壳聚糖与水杨醛的质量比为1:4~8，控制加入速度，0.5~1h内加完，然后，加热至30...
【专利技术属性】
技术研发人员：冯辉霞，孔佩佩，陈娜丽，谭琳，赵丹，王跃毅，白德忠，
申请(专利权)人：兰州理工大学，
类型：发明
国别省市：甘肃,62