The invention belongs to the technical field of heat storage materials, and discloses an inorganic salt ceramic composite heat storage material. With the weight number, the heat storage materials were prepared by the following components: 24~32 K2CO3, 20~28 CaCO3, 6~10 BeO, 10~16 Si3N4, and 13~18 SiC. The material selection and proportion of the material are scientific and reasonable, the sintered material has an ultramicro porous structure. The thermal and mechanical properties of the material meet the requirements of industrial application: the melting temperature is 1200~1260 degrees C, the total heat storage capacity is 170 ~ 190J/g, and the maximum temperature of its use reaches 1300~1400.
【技术实现步骤摘要】
无机盐-陶瓷基复合储热材料及其制备方法
本专利技术属于储热材料
，具体涉及一种无机盐-陶瓷基复合储热材料及其制备方法。
技术介绍
储热复合材料从产生这一新的概念到现在，已经取得了明显的进展，为材料产品化及其在工业蓄热器和太阳能动力系统的应用提供基础依据。但原有的复合材料都在不同程度上存在一下问题盐类在固液相变过程中体积的缩胀会导致复合材料热阻的变化：熔盐蒸发将减少相变材料的份额，降低储热性能。本专利技术的目的就是要在以前研究结果的基础上改进无机盐复合储热材料的性能，研制出一种储热能力大、放热稳定和能避免或减少蒸发现象的材料：使其能在储热系统及蓄热器的应用中普及使用。
技术实现思路
本专利技术所要解决的第一个技术问题是提供一种无机盐-陶瓷基复合储热材料，以重量份数计，该储热材料由以下组分制备得到：K2CO324～32份、CaCO320～28份、BeO6～10份、Si3N410～16份和SiC13～18份。优选的，上述无机盐-陶瓷基复合储热材料，以重量份数计，该储热材料由以下组分制备得到：K2CO325～30份、CaCO322～25份、BeO6～8份、Si3N412...
【技术保护点】
无机盐‑陶瓷基复合储热材料，其特征在于，以重量份数计，该储热材料由以下组分制备得到：K2CO3 24～32份、CaCO3 20～28份、BeO 6～10份、Si3N4 10～16份和SiC 13～18份。
【技术特征摘要】
1.无机盐-陶瓷基复合储热材料，其特征在于，以重量份数计，该储热材料由以下组分制备得到：K2CO324～32份、CaCO320～28份、BeO6～10份、Si3N410～16份和SiC13～18份。2.根据权利要求1所述的无机盐-陶瓷基复合储热材料，其特征在于，以重量份数计，该储热材料由以下组分制备得到：K2CO325～30份、CaCO322～25份、BeO6～8份、Si3N412～15份和SiC15～18份。3.根据权利要求1或2所述的无机盐-陶瓷基复合储热材料，其特征在于，以重量份数计，该储热材料由以下组分制备得到：K2CO330份、CaCO325份、BeO6份、Si3N414份和SiC16份。4.权利要求1～3任一项所述无机盐-陶瓷基复合储热材料的制备方法，其特征在于，该方法具体包括以下步骤：(1)将K2CO324～32份、CaCO320～28份和BeO6～10份混合均匀，得到混合物1，按照质量比混合物1:无水乙醇:BeO瓷球＝1:0.11～0.14:0.05～0....
【专利技术属性】
技术研发人员：唐华，
申请(专利权)人：天津琪臻节能科技有限公司，
类型：发明
国别省市：天津,12