The invention relates to a biodegradable rice hull based composite material, including the following weight components: 500 portions of rice husk powder, 20 glass fiber 30 copies, 6 nano montmorillonite 4, 4 surface modifiers, 6 parts, 6 antioxidant 4, 110 polylactic acid, 130 copies of polylactic acid, thermoplastic resin 8 12, titanium dioxide 10 10, lubricants, and lubricants. 12 copies. The invention is based on clean and dry rice husk powder, and its raw materials are renewable, green and environmentally friendly. One dimension glass fiber, two-dimensional layered nano montmorillonite and three dimensional nanoscale titanium dioxide are added to ensure the rigidity and strength of the material, and the thermoplastic resin is used to enhance the toughness.
【技术实现步骤摘要】
一种可生物降解的稻壳粉基复合材料及其制备方法
本专利技术涉及高分子材料领域，尤其涉及的是一种可生物降解的稻壳粉基复合材料及其制备方法。
技术介绍
我国是农业大国，其中水稻种植面积世界最广。据不完全统计，我国每年稻壳产量达8000万吨，目前主要用于发电、制备白炭黑和活性炭、酿酒及化工原料等，但其中得到经济高效利用的比重很少。大量的稻壳因占地面积大，不得不掩埋或焚烧，造成资源严重浪费和环境污染问题。稻壳作为生物质材料，具有生物降解特性，目前利用其生物降解特性的研究主要是采用稻壳粉作为填充物，添加加到塑料中，以降低成本或提高材料的生物降解性能。主要问题在于稻壳粉的添加量少时，经济效益和生物降解特性改善不明显；当稻壳粉添加量较多时，加工流动性差，产品力学性能低，甚至无法成型。
技术实现思路
本专利技术的目的在于克服上述不足，提供一种以稻壳粉为主要基料，易于加工，具有优良力学性能的可生物降解的稻壳基复合材料。为实现上述目的，本专利技术的技术解决方案是：一种可生物降解的稻壳基复合材料，包括以下重量组分：稻壳粉500份、玻璃纤维20-30份、纳米蒙脱土4-6份、表面改性剂4-6份、...
【技术保护点】
一种可生物降解的稻壳基复合材料，其特征在于，包括以下重量组分：稻壳粉500份、玻璃纤维20‑30份、纳米蒙脱土4‑6份、表面改性剂4‑6份、抗氧剂4‑6份、聚乳酸110‑130份、热塑性树脂8‑12份、二氧化钛10‑15份、润滑剂10‑12份。
【技术特征摘要】
1.一种可生物降解的稻壳基复合材料，其特征在于，包括以下重量组分：稻壳粉500份、玻璃纤维20-30份、纳米蒙脱土4-6份、表面改性剂4-6份、抗氧剂4-6份、聚乳酸110-130份、热塑性树脂8-12份、二氧化钛10-15份、润滑剂10-12份。2.根据权利要求1所述可生物降解的稻壳基复合材料，其特征在于，热塑性树脂为EVA。3.根据权利要求1所述可生物降解的稻壳基复合材料，其特征在于，热塑性树脂为LLDPE。4.根据权利要求1所述可生物降解的稻壳基复合材料，其特征在于，表面改性剂为铝钛酸酯偶联剂。5.根据权利要求1所述可生物降解的稻壳基复合材料，其特征在于，抗氧剂为抗氧剂1010或抗氧剂168。6.根据权利要求1所述可生物降解的稻壳基复合材料，其特征在于，润滑剂为PE蜡或EVA蜡。7.权利要求1-6任一项所述可生物降解的稻壳基复合材料的制备方法，其...
【专利技术属性】
技术研发人员：王少会，庄展鹏，柯婵，
申请(专利权)人：壳氏黑龙江新材料科技有限公司，
类型：发明
国别省市：黑龙江,23
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。