The invention belongs to the production field of plastic gloves, in particular to a cold resistant PVC glove and a preparation method. The cold resistant PVC gloves include raw material for the following weight parts: PVC resin 70, 85 copies, CPE 10, 10 copies of modified chlorinated vinegar resin, 40 DOTP 55, 45 cold resistant plasticizer, 1 stabilizer 1.5, viscosity reducer 0, 35. Compared with ordinary PVC gloves, the glove of the invention has excellent cold resistance and can keep the softness of glove in low temperature environment. It is suitable for contact with low temperature objects or working in low temperature environment. The glove is formed by impregnation. The production process is simple and the cost is low, filling the air in the field of cold resistant PVC gloves. White, has a strong market competitiveness.
【技术实现步骤摘要】
一种耐寒PVC手套及其制备方法
本专利技术属于塑胶手套生产领域，具体涉及一种耐寒PVC手套及其制备方法。
技术介绍
PVC曾是世界上产量最大的通用塑料，广泛应用在建筑材料、地板革、管材、包装膜、发泡材料等各个方面。其中PVC手套以其不易过敏、成本低、耐腐蚀、化学稳定性好等优点而占据大部分市场份额。PVC为无定形结构的白色粉末，支化度较小，玻璃化温度77-90℃，树脂分子间是以很强的范德华力结合在一起的，刚性很强，柔软性不足，造成PVC树脂加工比较困难。为解决这些问题需要在PVC加工过程中引入增塑剂，增塑剂可以充于PVC大分子之间，使分子相互间的活动较容易，降低了聚合物分子链的结晶性，亦即增加了PVC树脂的塑性、曲绕性、柔韧性，而硬度、模量、玻璃化温度都下降，方便了PVC制品的加工成型。但是普通PVC手套加工成型后，玻璃化温度仍然很高，使得在低温下手套很硬，手感很差，难以进行精密操作。因此，研发出低温环境下仍能柔软有弹性的耐寒手套无疑具有十分重要的意义。
技术实现思路
本专利技术要解决的技术问题是研制出一种耐寒PVC手套，具体技术方案如下：一种耐寒PVC手套，包括以下重...
【技术保护点】
一种耐寒PVC手套，其特征在于，包括以下重量份的原料：PVC树脂 70‑85份；CPE10‑25份；改性氯醋树脂5‑10份；DOTP 40‑55份；耐寒增塑剂 30‑45份；稳定剂1‑1.5份；降粘剂20‑35份。
【技术特征摘要】
1.一种耐寒PVC手套，其特征在于，包括以下重量份的原料：PVC树脂70-85份；CPE10-25份；改性氯醋树脂5-10份；DOTP40-55份；耐寒增塑剂30-45份；稳定剂1-1.5份；降粘剂20-35份。2.根据权利要求1所述耐寒PVC手套，其特征在于：所述的CPE为含氯量25%-45%的氯化聚乙烯。3.根据权利要求1所述耐寒PVC手套，其特征在于：所述的改性氯醋树脂为氯乙烯、醋酸乙烯、乙烯醇三元共聚物。4.根据权利要求3所述耐寒PVC手套，其特征在于：所述的改性氯醋树脂三元共聚物中单体含量比为氯乙烯：醋酸乙烯：乙烯醇=82:13:5。5.根据权利要求1所述耐寒PVC手套，其特征在于：所述的耐寒增塑剂为己二酸二辛酯、癸二酸二辛酯、壬二酸二辛酯中的一种或者多种的混合物。6.根据权利要求1所述耐寒PVC手套，其特征在于：所述的稳定剂为液体钙锌稳定剂。7.根据权利要求6...