The present invention provides a method of chain expansion of polybutylene dibutylate, which is characterized by modifying the terminal of polybutylene dibutylene dibutylate to get a double bond end polyester by using the mercapto alkene reaction in clicking chemistry. After being dissolved in chloroform, two mercapto compound and photoinitiator were added, and then high molecular weight butanediol succinate was obtained after UV irradiation for a certain time. The method of the invention has the advantages of short time consumption, high efficiency and mild reaction conditions. The molecular weight of poly (butylene succinate) obtained by chain extension can be significantly improved compared with that before chain extension. The procedure is simple, the operation is convenient, and the practicality is strong.
【技术实现步骤摘要】
一种高效的聚丁二酸丁二醇酯扩链方法
本专利技术属于高分子材料合成领域，特别涉及一种高效的聚丁二酸丁二醇酯扩链方法。
技术介绍
聚丁二酸丁二醇酯(PBS)作为一种半晶质型热塑性塑料及生物降解型脂肪族聚酯，具有较好的生物可降解性能，优良的成型加工性能和良好的机械力学性能。其可加工性能接近于聚乙烯(PE)，物理性能接近于聚对苯二甲酸乙二醇酯(PET)。与聚己内酯(PCL)、聚羟基丁酸酯(PHB)、聚羟基脂肪酸酯(PHA)等降解塑料相比，PBS具有价格低廉、力学性能优异等特点；而与价格相近的聚乳酸(PLA)相比，PBS又具有加工方便，可适应目前常规的塑料加工工艺，耐热性能好的特点，其热变形温度可以超过100℃。目前，PBS已应用于生活生产、医药、农业等领域。随着高分子工业的发展及高分子材料的广泛应用，PBS的合成过程存在着一些问题，最为主要的问题是产物的分子量低，副产物多。目前国内外生产PBS一般都采用化学合成法。直接酯化法和酯交换法合成PBS在反应后期温度往往超过200℃，会出现脱羧、热降解等副反应，影响相对分子质量的提高并生成副产物。利用扩链法合成PBS聚合时间短，设...
【技术保护点】
一种聚丁二酸丁二醇酯的扩链方法，其特征在于，包括：以低分子量的、双端双键的聚丁二酸丁二醇酯为预聚物，在扩链剂和光引发剂存在的条件下，经紫外光照聚合，得到高分子量的聚丁二酸丁二醇酯。
【技术特征摘要】
1.一种聚丁二酸丁二醇酯的扩链方法，其特征在于，包括：以低分子量的、双端双键的聚丁二酸丁二醇酯为预聚物，在扩链剂和光引发剂存在的条件下，经紫外光照聚合，得到高分子量的聚丁二酸丁二醇酯。2.如权利要求1所述的方法，其特征在于，所述扩链剂为1,2-乙二硫醇、1,6-己二硫醇或1,8-辛二硫醇。3.如权利要求1所述的方法，其特征在于，所述光引发剂为安息香苯甲醚或Irgacure2959。4.如权利要求1所述的方法，其特征在于，所述预聚物、扩链剂和光引发剂的质量比为100：1～5：0.01～1。5.如权利要求1所述的方法，其特征在于，所述紫外光波长为...
【专利技术属性】
技术研发人员：高传慧，任秀，王博，刘月涛，季淑芳，王传兴，武玉民，
申请(专利权)人：青岛科技大学，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。