The present invention relates to a low viscosity two urea polyisocyanate and its preparation method. The low viscosity two urea polyisocyanate contains urea two ketone and two urea base, and the molar ratio of the urea two ketone with the contraction two urea group is 0.01 0.80. The preparation method is to use phosphine compounds to catalyze the two polymerization of diisocyanate first, to get some isocyanate oligomers containing two ketone groups with urea, and then the reaction system is added to the catalyst and water to get the two urea polyisocyanate. The viscosity of the two urea polyisocyanate prepared by this method is low, the chroma is lower than 20Hazen, and the conversion rate of diisocyanate material is significantly improved.
【技术实现步骤摘要】
一种低粘度缩二脲聚异氰酸酯及其制备方法和用途
本专利技术涉及一种低粘度缩二脲聚异氰酸酯及其制备方法，所述的低粘度缩二脲聚异氰酸酯可以用于聚氨酯涂料用固化剂。
技术介绍
聚氨酯涂料以其施工温度范围宽、柔韧性好、附着力强等优良的性能而在汽车原厂漆、汽车修补漆、塑胶漆、工业漆、木器漆、皮革漆等领域获得了广泛的应用。聚氨酯涂料用二异氰酸酯工业化产品主要有HDI、IPDI、TDI和XDI等，分为脂肪族异氰酸酯和芳香族异氰酸酯。脂肪族异氰酸酯类固化剂耐黄变性好，目前市场上基于HDI的异氰酸酯固化剂主要为HDI三聚体和HDI缩二脲这两种产品，其中基于HDI缩二脲涂膜的柔韧性和附着力尤其卓越。近年来，降低涂料挥发性有机化合物的排放量已经成为发展趋势，高固体分涂料是降低涂料挥发性有机化合物排放量的一个重要发展方向，可降低聚异氰酸酯和多元醇的粘度，以制备高固体分双组分聚氨酯涂料。缩二脲聚异氰酸酯可以由多异氰酸酯与水、胺或可原位产生水的试剂反应制备，但常规工艺制备的缩二脲粘度很高，需要进行稀释使用。HDI缩二脲25℃时的粘度大于8000cP，使用时通常用有机溶剂进行稀释，如二甲苯、乙二...
【技术保护点】
一种低粘度缩二脲聚异氰酸酯，其特征在于，包含脲二酮基和缩二脲基且所述脲二酮基与缩二脲基的摩尔比例为0.01‑0.80，优选0.02‑0.60。
【技术特征摘要】
1.一种低粘度缩二脲聚异氰酸酯，其特征在于，包含脲二酮基和缩二脲基且所述脲二酮基与缩二脲基的摩尔比例为0.01-0.80，优选0.02-0.60。2.根据权利要求1所述的低粘度缩二脲聚异氰酸酯的制备方法，其包括如下步骤：二异氰酸酯先发生二聚反应，得到部分含脲二酮基团的异氰酸酯低聚物，然后向反应体系加入催化剂和水进行缩二脲化反应，生成缩二脲聚异氰酸酯。3.根据权利要求2所述的制备方法，其特征在于，二聚反应阶段，二异氰酸酯单体的转化率为3-30％，优选5-25％。4.根据权利要求2或3所述的制备方法，其特征在于，整个反应过程二异氰酸酯单体的转化率为32-80％，优选35-70％。5.根据权利要求2-4中任一项所述的制备方法，其特征在于，二异氰酸酯的二聚反应在膦类催化剂存在下进行，所述的膦类催化剂选自氨基取代膦、三烷基膦、环烷基膦，优选氨基取代膦，例如三(二甲氨基)膦、三(二乙氨基)膦，更优选三(二甲氨基)膦；基于二异氰酸酯单体质量计算，膦类催化剂的用量为0.02-4wt％，优选0.05-3wt％。6.根据权利要求2-5中任一项所述的制备方法，其特征在于，二异氰酸酯二聚反应阶段的温度为20-...
【专利技术属性】
技术研发人员：王彪，尚永华，石滨，朱智诚，李海军，侯文才，李文滨，华卫琦，
申请(专利权)人：万华化学集团股份有限公司，
类型：发明
国别省市：山东,37