一种发泡砖及其制作方法技术

本发明专利技术公开了一种发泡砖，由以下原料按重量份配比：淤沙20‑30份、粉煤灰10‑20份、蛭石1‑2份、玻璃纤维丝8‑10份、石墨0.5‑1份、硅灰石5‑10份、生石灰10‑15份、氧化锌3‑5份、高岭土5‑10份、低温玻璃粉5‑8份和抑制剂1‑2份。本发明专利技术以廉价的资源为主要原料且工艺简单，成本低。本发明专利技术的发泡砖具有机械强度较高高、密度小、保温性能好，且化学稳定性高、耐久性好。可制成各类管材、板材，可广泛应用于建筑保温隔声和化工管道保温等领域。

A kind of foamed brick and its making method

The invention discloses a foamed brick with the following raw materials according to the weight ratio: silt 20, 30 copies of fly ash 10, 1 vermiculite 2, 8 glass fiber 10, 0.5 graphite, 1, 5, limestone, lime 10, Zinc Oxide, kaolin, low temperature glass powder and inhibitor 2 copies. The invention takes cheap resources as the main raw material, and has simple process and low cost. The foaming brick has the advantages of high mechanical strength, small density, good heat preservation performance, high chemical stability and good durability. It can be made into various kinds of pipes and plates, and can be widely applied to the fields of building insulation, sound insulation and chemical pipe insulation.

【技术实现步骤摘要】
一种发泡砖及其制作方法
本专利技术涉及建筑材料
，特别涉及一种发泡砖及其制作方法。
技术介绍
随着建筑节能的推广和人们对居住环境舒适性需求的不断提高，保温材料越来越受到人们的广泛重视，作为房屋保温材料之一的常温免烧发泡砖，主要是由水泥、矿渣粉、河砂为生产原材料，拌和后经压力空气发泡，强制将空气拌入混合浆内型成，微气泡结构的混凝土浇模成型，经蒸压反应等工序制作而成，是一种环保、节能、材质稳定的新型墙体材料。由于其保温、隔音、防火、强度优于传统保温材料，越来越受人们的欢迎，然而现有的发泡砖使用的原料成本较高，由于生产成本较高，所以售卖的价格相对较高，使其市场的占有率收到了一定的限制。为此，我们提出一种发泡砖及其制作方法。
技术实现思路
本专利技术的主要目的在于提供一种发泡砖及其制作方法，可以有效解决
技术介绍
中的问题。为实现上述目的，本专利技术采取的技术方案为：一种发泡砖，由以下原料按重量份配比：淤沙20-30份、粉煤灰10-20份、蛭石1-2份、玻璃纤维丝8-10份、石墨0.5-1份、硅灰石5-10份、生石灰10-15份、氧化锌3-5份、高岭土5-10份、低温玻璃粉5-8份和抑制剂1-本文档来自技高网...

【技术保护点】
一种发泡砖，其特征在于，由以下原料按重量份配比：淤沙20‑30份、粉煤灰10‑20份、蛭石1‑2份、玻璃纤维丝8‑10份、石墨0.5‑1份、硅灰石5‑10份、生石灰10‑15份、氧化锌3‑5份、高岭土5‑10份、低温玻璃粉5‑8份和抑制剂1‑2份。

【技术特征摘要】
1.一种发泡砖，其特征在于，由以下原料按重量份配比：淤沙20-30份、粉煤灰10-20份、蛭石1-2份、玻璃纤维丝8-10份、石墨0.5-1份、硅灰石5-10份、生石灰10-15份、氧化锌3-5份、高岭土5-10份、低温玻璃粉5-8份和抑制剂1-2份。2.根据权利要求1所述的一种发泡砖，其特征在于：所述原料按以下重量份配比：淤沙25份、粉煤灰15份、蛭石1.5份、玻璃纤维丝9份、石墨0.8份、硅灰石7份、生石灰13份、氧化锌4份、高岭土8份、低温玻璃粉6份和抑制剂1.5份...

【专利技术属性】
技术研发人员：孙坚强，吕幼牧，史昌宝，
申请(专利权)人：安徽建鑫新型墙材科技有限公司，
类型：发明
国别省市：安徽,34