一种有机锡卤化合物发光材料的制备及应用制造技术
Preparation and application of an organotin halide compound luminescent material
The present invention provides a preparation method of organic tin halogen compound luminescent material, which includes: Step 1: dissolve tin source compound and organic amine compound in organic solvent and obtain solution A; step 2: add organic solvent B in solution A, settle precipitate, pour out supernatant, and get solid dry Dryness, obtained the organic tin halogen compound luminescent material. The organotin halide compound has no toxicity, cheap, simple preparation process and more than 80% fluorescence quantum yield under ultraviolet light, and the composite organic polymer block based on the material can be used for the preparation of light emitting devices.
【技术实现步骤摘要】
一种有机锡卤化合物发光材料的制备及应用
本专利技术涉及一种新型有机锡卤发光材料的合成与应用，属于有机-无机杂化材料的合成与荧光材料领域。
技术介绍
随着世界人口的不断增长和社会经济的快速发展。寻求和开发节能，环保，高效的工程材料是可持续发展的必要条件。在显示照明领域，高亮度，高量子产率的发光材料是节能环保灯具的重要组成部分并得到广泛的关注。自低压汞灯问世以来，科学家开发了大量的荧光材料用于实现紫外线激发下的发光照明。相比传统的白炽灯，其能耗成本有显著降低，现已广泛被市场所认可。目前，商用的荧光粉材料多为稀土基无机材料，存在原料成本高，毒性大等问题。采用廉价无毒元素制备高质量荧光粉成为该领域的一大挑战。
技术实现思路
本专利技术的目的在于提供一种有机锡卤杂化材料的制备及应用。为了达到上述目的，本专利技术提供了一种有机锡卤化合物发光材料的制备方法，其特征在于，包括：步骤1：将锡源化合物以及有机胺化合物溶解于有机溶剂中，得到溶液A；步骤2：在溶液A中加入有机溶剂B，静置沉淀，倾倒出上层清液，将所得固体干燥，得到有机锡卤化合物发光材料。优选地，所述的步骤2中在倾倒出上层清液后...
【技术保护点】
一种有机锡卤化合物发光材料的制备方法，其特征在于，包括：步骤1：将锡源化合物以及有机胺化合物溶解于有机溶剂中，得到溶液A；步骤2：在溶液A中加入有机溶剂B，静置沉淀，倾倒出上层清液，将所得固体干燥，得到有机锡卤化合物发光材料。
【技术特征摘要】
1.一种有机锡卤化合物发光材料的制备方法，其特征在于，包括：步骤1：将锡源化合物以及有机胺化合物溶解于有机溶剂中，得到溶液A；步骤2：在溶液A中加入有机溶剂B，静置沉淀，倾倒出上层清液，将所得固体干燥，得到有机锡卤化合物发光材料。2.如权利要求1所述的有机锡卤化合物发光材料的制备方法，其特征在于，所述的步骤2中在倾倒出上层清液后，将所得的固体用有机溶剂B洗涤，再将所得固体干燥，得到有机锡卤化合物发光材料。3.如权利要求1所述的有机锡卤化合物发光材料的制备方法，其特征在于，所述的步骤1中的锡源化合物为二氯化锡、二溴化锡以及二碘化锡的一种或几种；所述的步骤1中的有机胺化合物的结构式为RCH2CH2CH2NH2·HBr，其中R＝H，CH3CH2，NH2CH2CH2或CH3CH2CH2CH2。所述的有机溶剂是DMSO、DMF和乙腈中的一种或几种。4.如权利要求1所述的有机锡卤化合物发光材料的制备方法...
【专利技术属性】
技术研发人员：宁志军，龚晋慷，付鹏飞，尚跃群，
申请(专利权)人：上海科技大学，
类型：发明
国别省市：上海,31