The present invention provides a diatom mud with visible light removal capacity, including the following quality components: 20 diatomite 48 copies, 15 copies of latex powder 3, 10 nanoscale Ag Fe2O35, 10 nanoscale Ag, 10 bentonite 30, 30 montmorillonite, 5 calcium silicate, inorganic pigment 1 5, dispersant 3 copies. The nano Ag Fe2O3 and Ag WO3, which have visible light degradation characteristics, are used as visible light catalysts to be added to the porous structure of diatom mud to realize the enrichment of organic gases in diatom mud, and the catalytic degradation of organic gases can be realized by using visible light catalytic properties, and the deficiency of traditional catalysts is avoided.
【技术实现步骤摘要】
具有可见光去除能力的硅藻泥及其应用
本专利技术属于无机材料领域，具体涉及一种含有纳米氧化物的无机多孔材料及其方法。
技术介绍
硅藻泥的主要成分是硅藻土，硅藻土化学成分以SiO2为主，矿物成分为蛋白石及其变种。硅藻土的密度为1.9～2.3g/cm3，比表面积为40～65m2/g，孔体积0.45—0.98m3/g，因而具有疏松多孔、容易吸水的性质，吸水率是自身体积的2～4倍，加水即成为硅藻泥。专利CN106348700A将硅藻土与石英粉、氧化钙、苯甲酸钠、纤维素以及可再分散乳胶粉组合，制为室内涂装涂料；专利CN106220046A将硅藻土30％-45％与可再分散乳胶粉4％-10％、高岭土10％-15％、熟胶粉3％-5％、纤维素5％-10％、膨润土3％-10％、纳米二氧化钛5％-10％、纳米二氧化锌5％-10％，得到吸附性能好、空气净化效果好的材料。目前传统的硅藻泥利用其多孔特点，能够有效吸附有机污染物，但是由于硅藻泥本身无对有机污染物降解功能，故只能吸附有机污染物，而不能在富集污染物的同时，将污染物降解，实现有害气体的完全去除。
技术实现思路
针对本领域存在的不足之处，本...
【技术保护点】
一种具有可见光去除能力的硅藻泥，其特征在于，包括以下质量份的成分：硅藻土20‑48份，可再分散乳胶粉3‑15份，纳米Ag‑Fe2O35‑10份，纳米Ag‑WO35‑10份，膨润土10‑30份，蒙托土5‑30份，轻钙5‑20份，无机颜料1‑5份，分散剂1‑3份。
【技术特征摘要】
1.一种具有可见光去除能力的硅藻泥，其特征在于，包括以下质量份的成分：硅藻土20-48份，可再分散乳胶粉3-15份，纳米Ag-Fe2O35-10份，纳米Ag-WO35-10份，膨润土10-30份，蒙托土5-30份，轻钙5-20份，无机颜料1-5份，分散剂1-3份。2.根据权利要求1所述的硅藻泥，其特征在于，包括以下质量份的成分：500-800目的硅藻土20-40份，可再分散乳胶粉10-15份，纳米Ag-Fe2O35-10.份，纳米Ag-WO35-10份，膨润土15-20份，蒙托土15-20份，轻钙10-20.份，无机颜料1-3份，分散剂1份。3.根据权利要求1所述的硅藻泥，其特征在于，所述分散剂为石蜡、硬脂酸锌、三聚磷酸钠中的一种或多种。4.根据权利要求1-3任一项所述的硅藻泥，其特征在于，所述纳米Ag-Fe2O3采用光致还原的方法制备，包括操作：将硝酸银溶解在乙二醇中，配制为硝酸银的乙二醇溶液；将Fe2O3粉末分散在所述乙...
【专利技术属性】
技术研发人员：刘岗，刘杰，郑康，陈林，田兴友，
申请(专利权)人：中国科学院合肥物质科学研究院，
类型：发明
国别省市：安徽,34