The invention provides a special thick steel plate for the structural module of a PWR nuclear power plant and its manufacturing method. The composition of the steel plate is as follows: 0.16 C, 0.22, 0.42%, 1.10, 1.60%, P, less than 0.010%, less than 0.005%, Cr, 0.30% of 0.30%, 0.60, 0.80% of Mo; 0.020 0.020 0.045%. Al; 0.30 Ni 0.50; the rest are Fe and unavoidable impurities. Method package smelting continuous casting vacuum compound welding - slab heating rolling - straightening - stacking slow cooling - heat treatment - Ultrasonic testing - cutting edge - inspection, checking - into storage, the products produced by this invention have good comprehensive mechanical properties, and the shrinkage of the Z section of steel plate thickness at 1/2 and 1/4 is up to 65% Above\u3002
【技术实现步骤摘要】
一种压水堆核电站结构模块用特厚钢板及其制造方法
本专利技术属于金属材料领域，尤其涉及一种压水堆核电站结构模块用特厚钢板及其制造方法。
技术介绍
为了保障国民经济的稳步发展，我国正在酝酿规模更大的核电建设计划，而非能动压水堆核电站AP1000作为典型的第三代核电站，是今后我国核电机组建设的主要堆型。尽管核电站的模块化建设已经在国内以往的核电建设中有所体现，但AP1000核电站则将模块的规模和数量做到了最大化，实现了“模块”到“模块化”质的飞跃。正是由于AP1000第三代先进压水堆核电机组采用了大规模模块化的设计、施工技术，所以才能够保证核电站施工质量的同时，大大缩短了建设周期。每台AP1000核电机组需要模块数量为178个，其中结构模块108个，机械模块70个。建造如此多的结构模块和机械模块，需要钢铁材料的数量极大。由于对AP1000核电机组安全性要求更高，以及核电机组的装机容量日趋增大，对AP1000核电机组模块用钢也提出了更高的要求：一是厚度规格从最大厚度80mm扩到152mm，最大单重可达39吨；二是对钢板内部质量提出了更高的要求，增加了超声波探伤检测；三是增...
【技术保护点】
一种压水堆核电站结构模块用特厚钢板，其特征在于，该钢板的成分按重量百分比计如下：0.16‑0.25％的C；0.22‑0.42％的Si；1.10‑1.60％的Mn；≤0.010％的P；≤0.005％的S；0.10‑0.30％的Cr；0.60‑0.80％的Mo；0.020‑0.045％的Al；0.30‑0.50的Ni，其余为Fe和不可避免的杂质。
【技术特征摘要】
1.一种压水堆核电站结构模块用特厚钢板，其特征在于，该钢板的成分按重量百分比计如下：0.16-0.25％的C；0.22-0.42％的Si；1.10-1.60％的Mn；≤0.010％的P；≤0.005％的S；0.10-0.30％的Cr；0.60-0.80％的Mo；0.020-0.045％的Al；0.30-0.50的Ni，其余为Fe和不可避免的杂质。2.一种权利要求1所述的一种压水堆核电站结构模块用特厚钢板的制造方法，包冶炼—连铸—真空复合焊接—板坯加热—轧制—矫直—堆垛缓冷—热处理—超声波检测—切边—检验、检查—入库；其特征在于：(1)冶炼：采用RH进行真空处理，RH/VD循环时间≥10min，钢中[H]控制在2ppm以下、[O]控制在25ppm以下、[N]控制在35ppm以下；中间包目标过热度按小于20℃；全程保护浇...
【专利技术属性】
技术研发人员：孙殿东，李德刚，王永才，胡海洋，颜秉宇，王长顺，李文斌，王勇，王爽，李黎明，
申请(专利权)人：鞍钢股份有限公司，
类型：发明
国别省市：辽宁,21