A conductive metal organic frameworks for resistive gas sensors
The indium based conductive metal organic skeleton material and its preparation method used in the resistance gas sensor belong to the cross field of chemical, material science and electronic science. The New Indium based conductive metal organic framework material has regular periodic framework structure and controllable particle size. The method is easy to operate, cost saving, and has important application in the technology field of assembling resistance gas sensors. The assembled resistance gas sensor has the characteristics of wide response range, fast response speed, good repeatability and room temperature operation, especially the selective sensing of volatile organic amine harmful substances.
【技术实现步骤摘要】
一种应用于电阻式气体传感器的导电金属有机骨架材料
本专利技术属于化学、材料和电子等
，具体涉及一种稳定的导电金属有机骨架材料制备方法及气体传感应用。
技术介绍
气体传感在工业生产、过程控制、环境监测、食品质量检测、医疗分析方面具有重要应用。目前，气体传感材料种类很多，例如：陶瓷材料、半导体材料、聚合物材料等。但是，探索适应实际应用的高响应的气体传感材料仍然是一种挑战，特别是在商业领域。半导体和陶瓷材料的响应和恢复能力强，但是，浓度和阻抗之间的线性关系并不理想，与此相比，其他材料的响应、恢复都相对较慢。因此，开发响应速度快、恢复能力强、可测范围广、选择性好的气体传感材料已成为传感领域的迫切需求。金属有机骨架材料(MOFs)是一类由无机金属节点和有机桥连配体通过配位自组装得到的具有周期性结构的新型纳米多孔材料,它兼具了无机和有机材料的性能。MOFs具有大的比表面积，多孔性，敞开的窗口和化学成分稳定等诸多性能,因此它具备了其它无机多孔材料所不能比拟的优势。MOFs具有丰富的化学组成，结构中的官能团具有多种多样的功能性从而利于实现其预期功能，而且MOFs在许多方面有...
【技术保护点】
一种应用于电阻式气体传感器的导电金属有机骨架材料的制备方法，其特征在于包括以下具体步骤：(1)将铟盐、有机配体9,10‑二(乙炔基间苯二酸)蒽按照1～2：0.5～10的摩尔比加入到密闭反应釜，再加入一定量的有机溶剂、水、酸；(2)然后将反应釜放在80℃～120℃的条件下，反应48～170h后得到一种新型的铟基金属有机骨架晶体材料。
【技术特征摘要】
1.一种应用于电阻式气体传感器的导电金属有机骨架材料的制备方法，其特征在于包括以下具体步骤：(1)将铟盐、有机配体9,10-二(乙炔基间苯二酸)蒽按照1～2：0.5～10的摩尔比加入到密闭反应釜，再加入一定量的有机溶剂、水、酸；(2)然后将反应釜放在80℃～120℃的条件下，反应48～170h后得到一种新型的铟基金属有机骨架晶体材料。2.按照权利要求1的应用于电阻式气体传感器的导电金属有机骨架材料的制备方法，其特征在于：铟盐、有机配体、有机溶剂、酸的摩尔比为：1:0.1～10:0.1～10:0.1～10。3.按照权利要求1的应用于电阻式气体传感器的导电金属有机骨架材料的制备方法，其特征在于：所选的有机溶剂包括N,N-二甲基甲酰胺、二甲亚砜、N,N-二甲基乙酰胺和N,N-二乙基甲酰胺中的一种。4.按照权利要求1的应用于电阻式气体传感器的导电金属有机骨架材料的制备方法，其特征在于：所选的酸为...