本发明专利技术公开一种织物染色的方法，包括以下步骤：将织物置于染缸中进行染色，得色织物半成品；将所述色织物半成品置于pH为5～6的醋酸溶液中，于42℃～48℃保温5min～15min，然后加入柔软剂继续保温5min～15min；再加入亲水性固色剂继续保温10min～20min，出缸，烘干，即得色织物。采用本方法能明显改善色织物的亲水性能，所得色织物的亲水性合格率达97％以上。

Fabric dyeing method and color fabric

The present invention discloses a method of dyeing fabric, which includes the following steps: dyeing the fabric in a dyed tank and dyeing the semi finished product; placing the semi finished fabric in the acetic acid solution of pH 5~6, holding 5min to 15min at 42 to 48 C, then adding softener to continue the heat preservation 5min to 15min, and then adding hydrophilic solid. Continue to keep the color agent 10min ~ 20min, out of the cylinder, drying, that is, dyed fabric. This method can obviously improve the hydrophilicity of the yarn dyed fabric, and the qualified rate of the dyed fabric is more than 97%.

【技术实现步骤摘要】
织物染色的方法及色织物
本专利技术涉及织物染色生产
，特别涉及一种织物染色的方法及色织物。
技术介绍
在针织物的染色生产过程中和功能性整理时，要求针织物有良好的渗透性和亲水性，这样才可以通过介质将化工料附着在织物上，完成染色和功能性整理，因此提高织物的亲水性效果十分重要。目前，提高针织物的亲水性能研究主要有两类：一是物理方法：通过与亲水性物质共混或复合纺丝提高纤维的亲水性，或进行纤维微孔化处理和纤维截面异形化提高纤维表面的水润湿性能；二是化学方法：通过引入亲水单体嵌段共聚使大分子具有亲水性，或通过亲水性单体接枝共聚在纤维表面进行亲水化整理，接枝共聚方法可以纯化学反应，也可以借助等离子体、紫外照射改性、酶处理改性等手段。但是，传统的方法要么效果不明显，要么工艺复杂。
技术实现思路
基于此，有必要提供一种织物染色的方法，可以明显提高针织物的亲水性，且其工艺简单。一种织物染色的方法，包括以下步骤：将织物置于染缸中进行染色，得色织物半成品；将所述色织物半成品置于pH为5～6的醋酸溶液中，于42℃～48℃保温5min～15min，然后加入柔软剂继续保温5min～15min；再加入亲水性固色剂本文档来自技高网...

【技术保护点】
一种织物染色的方法，其特征在于，包括以下步骤：将织物置于染缸中进行染色，得色织物半成品；将所述色织物半成品置于pH为5～6的醋酸溶液中，于42℃～48℃保温5min～15min，然后加入柔软剂继续保温5min～15min；再加入亲水性固色剂继续保温10min～20min，出缸，烘干，即得色织物。

【技术特征摘要】
1.一种织物染色的方法，其特征在于，包括以下步骤：将织物置于染缸中进行染色，得色织物半成品；将所述色织物半成品置于pH为5～6的醋酸溶液中，于42℃～48℃保温5min～15min，然后加入柔软剂继续保温5min～15min；再加入亲水性固色剂继续保温10min～20min，出缸，烘干，即得色织物。2.根据权利要求1所述的织物染色的方法，其特征在于，所述柔软剂的加入量与所述醋酸溶液的质量体积比为0.1g～4g:1L。3.根据权利要求1所述的织物染色的方法，其特征在于，所述柔软剂选自季铵盐改性聚硅氧烷和可溶性聚氨酯类柔软剂中的至少一种。4.根据权利要求1所述的织物染色的方法，其特征在于，所述亲水性固色剂的加入量与所述醋酸溶液的质量体积比为1g～4g:1L。5.根据权利要求1所述的织物染色的方法，其特征在于，所述亲水性固色剂为阳离子型亲水性固色...

【专利技术属性】
技术研发人员：刘丽军，李华南，黄宇光，
申请(专利权)人：广东溢达纺织有限公司，
类型：发明
国别省市：广东,44