一种酸化改性白烟灰复合盐基亚磷酸铅助剂及其制备方法技术
Acidification modified white smoke ash composite salt base lead phosphite auxiliary and preparation method thereof
The present invention discloses a kind of acid modified white smoke compound salt base phosphite additive, which uses the white smoke and phosphorus trichloride collected from the copper smelting process as raw material, and reacts to remove the soluble metal ions under the catalysis of glacial acetic acid, and modifier the insoluble metal ions to produce the precipitate, and filter it through filtration. A finished product. The invention adopts industrial waste residue as raw material, and its raw material is widely and inexpensive; the preparation method is simple and reasonable, and avoids the poisoning caused by lead dust in production and use, and the product has good performance and is suitable for industrial production.
【技术实现步骤摘要】
一种酸化改性白烟灰复合盐基亚磷酸铅助剂及其制备方法
本专利技术具体涉及一种酸化改性白烟灰复合盐基亚磷酸铅助剂及其制备方法。
技术介绍
二盐基亚磷酸铅是一种白色或微黄色粉末。由于其具有耐候性、热稳定性、电绝缘性等优良性能，并有抗氧化性和屏蔽紫外线的性能。因而广泛用作为聚氯乙烯和聚氯乙烯/聚乙烯共聚物的热稳定剂，特别是室外用电缆、建筑用板材、瓦楞板、管材等不透明硬质和软质制品。传统的二盐基亚磷酸铅是以青铅、醋酸、液碱及亚磷酸为原料生产，或以氧化铅和亚磷酸为原料生产，生产工艺复杂，成本较高，且在使用中粉尘大，计量次数多，易发生计量误差，对型材质量影响大，有污染，粉尘吸入人体有毒性。白烟灰是火法炼铜的熔炼过程中，在造锍和吹炼两阶段产生的含尘烟气，经过余热锅炉、旋涡收尘器、排烟机及电收尘器后，得到的含有大量铜、锌、铅等多种有价金属的白色烟灰。该烟灰富含有铜、铅、锌、砷、铋、锑、铟等多种有价金属，对于这种富含有价金属的烟尘，目前大多数综合利用方法以水浸和稀硫酸浸出白烟灰中的铜和锌等可溶性金属，再利用不同的方法分别处理浸出液和浸出渣。但由于受原料、工艺方法、工艺条件的影响，铜熔...
【技术保护点】
一种酸化改性白烟灰复合盐基亚磷酸铅助剂，其特征在于：采用铜熔炼过程产生的经电收尘收集的白烟灰和三氯化磷为原料，在冰醋酸的催化作用下反应脱除可溶性金属离子，并对其不溶的金属离子改性生成沉淀物，经过过滤、干燥得到的成品。
【技术特征摘要】
1.一种酸化改性白烟灰复合盐基亚磷酸铅助剂，其特征在于：采用铜熔炼过程产生的经电收尘收集的白烟灰和三氯化磷为原料，在冰醋酸的催化作用下反应脱除可溶性金属离子，并对其不溶的金属离子改性生成沉淀物，经过过滤、干燥得到的成品。2.根据权利要求1所述的一种酸化改性白烟灰复合盐基亚磷酸铅助剂，其特征在于：所述复合盐基亚磷酸铅助剂中各种物料用量中的重量份数为：白烟灰3-5份，水1份，冰醋酸0.005-0.002份，三氯化磷0.6-2份。3.根据权利要求1或2所述的一种酸化改性白烟灰复合盐基亚磷酸铅助剂，其特征在于：所述复合盐基亚磷酸铅助剂是通过浸出反应结束后的固体产物经过100-120℃温度的干燥得到。4.根据上述任一权利要求所述的一种酸浸改性白烟灰复合盐基亚磷酸铅助剂的制备方法，其特征在于：包括以下步骤：a、将水、采用铜熔...