The invention discloses a water-soluble quantum epoxy acrylic emulsion, which is mainly made of the following raw material with a mass fraction of 30 acrylate monomers, 90 initiators, 0.1 initiators, 5 copies, 1 4C units alcohol 15, 40 epoxy resin 1, 5 inorganic nanomaterials, 15 copies of inorganic nanomaterials, and 1 20 of water 1. Accordingly, the invention also discloses a preparation method and application of water-soluble quantum epoxy acrylic emulsion. Using the invention, the water-soluble quantum epoxy acrylic emulsion is environmentally friendly and energy saving, and greatly improves the water resistance, salt spray resistance, hardness, and metal and glass adhesion.
【技术实现步骤摘要】
水溶性量子环氧丙烯酸乳液及其制备方法和应用
本专利技术涉及表面保护漆
，特别涉及一种水溶性量子环氧丙烯酸乳液及其制备方法，以及水溶性量子环氧丙烯酸乳液在金属漆和非金属漆中的应用。
技术介绍
随着环保要求的日益严格，现已开发出来的水溶性丙烯酸树脂被得到重视。现有的水溶性丙烯酸树脂制备，将由自由基聚合得到的可溶于水的丙烯酸树脂溶解在40-80％wt水中，得到不含有机溶剂的水溶性丙烯酸树脂。此种水溶性丙烯酸树脂既保留了溶剂型丙烯酸树脂所配制成的涂料诸多优点，如流平好、光泽高、成膜佳及涂膜致密性好，又显著改善树脂在生产、储存、运输及使用过程中的消防安全性、环境保护性，还减少有机溶剂的消耗、降低生物毒害性等。然而由于其分子结构中含有较大量的强亲水性羧基，导致其所配制的涂料干燥成膜后涂层耐水性不够理想，常温下水浸泡十至二十分钟，涂层即会发生溶解，并且在玻璃板上涂层附着力较低，仅为二至三级，热塑性水溶性丙烯酸树脂的硬度，在HB以下，上述缺陷导致其不能满足玻璃涂层耐水性、附着力达到一级以上、硬度2H以上、耐水煮1小时无涂层脱落现象的使用要求。而且，现有丙烯酸树脂用于金属漆时...
【技术保护点】
一种水溶性量子环氧丙烯酸乳液，其特征在于，其主要由下述以质量份计的原料制成：
【技术特征摘要】
1.一种水溶性量子环氧丙烯酸乳液，其特征在于，其主要由下述以质量份计的原料制成：2.如权利要求1所述的水溶性量子环氧丙烯酸乳液，其特征在于，所述丙烯酸酯类单体选用合成溶剂型丙烯酸树脂的丙烯酸酯类单体；所述1-4C单元醇选用异丙醇、异丁醇、乙醇、正丁醇中的一种或多种；所述无机纳米材料为纳米二氧化硅、纳米二氧化钛、气相纳米二氧化铝中的一种或多种。3.如权利要求1所述的水溶性量子环氧丙烯酸乳液，其特征在于，所述丙烯酸酯类单体选用含羧基的强亲水性丙烯酸酯类单体，所含羧基的强亲水性丙烯酸单体用量占丙烯酸酯单体总量的5-40wt％，所述含羧基的强亲水性丙烯酸酯类单体包括丙烯酸、甲基丙烯酸、顺丁烯二酸。4.如权利要求1所述的水溶性量子环氧丙烯酸乳液，其特征在于，还包括：中和剂1-7份；所述中和剂选用有机胺或无机氨。5.如权利要求1所述的水溶性量子环氧丙烯酸乳液，其特征在于，还包括：消泡剂1-5份；杀菌剂1-5份。6.一种制备如权利要求1-5任一项所述的水溶性量子环氧丙烯酸乳液的方法，其特征在于，包括:(一)将丙烯酸酯类单体、75-95％引发剂按配方混合搅拌溶解均匀，得到混合溶液；(二)将1-4C单元醇、环氧树脂、无机...
【专利技术属性】
技术研发人员：郑伟洲，
申请(专利权)人：广东海特高新材料有限公司，
类型：发明
国别省市：广东,44