The present application discloses a sidewalk brick made of aluminum ash and residue, which is made of a variety of raw materials, including 45~60 parts of aluminum ash residue, 5~10 parts of lime, 3~5 plaster, 8~12 plaster, 10~20 ordinary portland cement, 2~5 micro silicon powder and 5~10 engineering sand. The high performance water reducing agent is 0.5% to 1% of the sum of the cement and the added lime, and the rock sand crystals are 1% ~ 1.5% of the quality of the common portland cement and the added lime. The calcium formate is 0.5% ~ 1% of the quality of the common portland cement and the described lime, and the residue of the aluminum ash residue is used for production. Low cost features. Effectively reducing the impact of aluminum ash accumulation on the ecological environment has played an important role in the regeneration and utilization of resources and has important practical value.
【技术实现步骤摘要】
用铝灰渣残灰制备的人行道砖
本公开一般涉及制砖领域，具体涉及制备人行道砖的
，尤其涉及一种用铝灰渣残灰制备的人行道砖。
技术介绍
随着我国经济的迅猛发展，对铝的需求量持续增加。我国已经成为世界最大的铝生产国家。随着金属铝的广泛应用，铝灰的产生量也不断增加。铝灰是电解铝或铸造铝生产工艺中产生的熔渣经冷却加工后的产物，是可再生资源。目前我国铝灰的处理方式还主要以堆积为主，一方面堆渣占用了大量的土地，另一方面大量的铝灰在填埋时未经过无害化处理，导致环境污染。铝灰中含有铝及多种有价元素，主要由金属铝单质、氧化物、氯化物等等构成。其中氮化铝在堆积时易与水发生反应，生成氨气。氨气是一种无色有刺激性恶臭气味的气体，因此大大增加了铝灰回收利用的难度。铝灰的来源主要有以下2方面：一方面是在电解氧化铝工艺生产过程中，由于操作和测定器具的携带、阳极更换、出铝、铸锭以及电解槽大修时产生。另一方面是原铝锭、铝材、铝压铸件与铸件、再生铝生产中，熔炼与铸造是必不可少的关键性工序，在此工序中定会产生一定量的铝灰，其中铝灰中金属铝的质量分数为30％～50％。刚出炉的铝灰含有大量的金属铝，基于...
【技术保护点】
一种用铝灰渣残灰制备的人行道砖，使用多种原料制成，其特征在于，所述原料包括以下质量份数的组分：铝灰渣残灰45～60份、生石灰5～10份，石膏3～5份、熟石灰8～12份、普通硅酸盐水泥10～20份、微硅粉2～5份、工程砂5～10份，高性能减水剂为所述普通硅酸盐水泥和所述熟石灰之和的0.5％～1％，岩砂晶为所述普通硅酸盐水泥和所述熟石灰质量之和的1％～1.5％，甲酸钙为所述普通硅酸盐水泥和所述熟石灰质量之和的0.5％～1％。
【技术特征摘要】
1.一种用铝灰渣残灰制备的人行道砖，使用多种原料制成，其特征在于，所述原料包括以下质量份数的组分：铝灰渣残灰45～60份、生石灰5～10份，石膏3～5份、熟石灰8～12份、普通硅酸盐水泥10～20份、微硅粉2～5份、工程砂5～10份，高性能减水剂为所述普通硅酸盐水泥和所述熟石灰之和的0.5％～1％，岩砂晶为所述普通硅酸盐水泥和所述熟石灰质量之和的1％～1.5％，甲酸钙为所述普通硅酸盐水泥和所述熟石灰质量之和的0.5％～1％。2.根据权利要求...
【专利技术属性】
技术研发人员：倪红军，唐伟佳，吕帅帅，顾涛，汪兴兴，李志扬，
申请(专利权)人：南通大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。