The invention provides a preparation method for saving energy and waste gypsum blocks, in particular: mixing 5~8 copies of potassium methyl silicate, 0.5 to 2 portions of aluminum sulfate, 0.1 to 0.3 VAE emulsions, 0.5 to 1 diatomaceous earth, and 50~70 water, and then mixing with 1~5 pieces of waste particles to dry; then, dry. Dry waste pellets and 1~4 pieces of waste FRP powder are added to building gypsum slurry to make gypsum blocks. The invention improves the compatibility and binding force of the organic material and the gypsum inorganic material by means of chemical means, and can prepare the energy saving and thermal insulation gypsum block with various functions. The method of the invention improves the application of shoe making waste in gypsum building materials, opens up a new way of safe and effective use of the shoe waste, avoids the pollution to the environment and reduces the disposal cost.
【技术实现步骤摘要】
一种节能利废型石膏砌块的制备方法
本专利技术涉及一种制鞋废料在建筑材料中的应用方法，特别涉及一种制鞋废料在石膏建材中的应用方法。
技术介绍
制鞋行业每年产生大量的边角废料，主要是聚胺发泡塑料、聚脂纤维、橡胶、聚乙烯、聚丙烯、尼龙、树脂等有机高分子化合物，其中帮面的材料主要为纺织布料(包括棉布、腈纶、丙纶、氨纶、无纺布、复合网面布等)、皮革(天然皮、人造草皮、合成革皮等)、橡胶塑料和其他材料等，质量轻，密度小，体积大。目前，这种制鞋废料还没有有效的利用和处置方法，不但对堆放地的土壤、水体等生态环境造成很大危害，还存在巨大的火灾隐患。如采用填埋处理，不仅要占用大量土地，而且很难降解，还造成资源的浪费。如果用作锅炉燃料，会产生有毒烟气，污染环境，影响空气质量。如将废纤维回收或橡胶、塑料等再生利用，又存在品质繁杂、工业化利用困难及经济效益不好等诸多问题。因此，选择技术上可行、经济上合理的技术方案，如何更好地处理利用这些废料已经成为急需解决的问题。
技术实现思路
本专利技术提供了一种节能利废型石膏砌块的制备方法，将制鞋废料进行表面改性，提高制鞋废料中的有机材料与石膏无机材料的相...
【技术保护点】
一种节能利废型石膏砌块的制备方法，其特征在于具体包含以下步骤：1）将制鞋废料破碎成5mm以下的废料颗粒；2）按重量份数比，将5～8份的甲基硅酸钾、0.5～2份的硫酸铝、0.1～0.3份的VAE乳液、0.5～1份的硅藻土和50～70份的水制成混合液，加入到1～5份的上述废料颗粒中，拌合均匀后干燥备用；3）将步骤2）得到的废料颗粒和1～4份的废玻璃钢粉加入到建筑石膏料浆中，制成石膏砌块。
【技术特征摘要】
1.一种节能利废型石膏砌块的制备方法，其特征在于具体包含以下步骤：1）将制鞋废料破碎成5mm以下的废料颗粒；2）按重量份数比，将5～8份的甲基硅酸钾、0.5～2份的硫酸铝、0.1～0.3份的VAE乳液、0.5～1份的硅藻土和50～70份的水制成混合液，加入到1～5份的上述废料颗粒中，拌合均匀后干燥备用；3）将步骤2）得到的废料颗粒和1～4份的废玻璃钢粉加入到建筑石膏料浆中，制成石膏砌块。2.根据权利要求1所述的一种节能利废型石膏砌块的制备方法，其特征在于：所述的废玻璃钢粉由热固性废玻璃钢经破碎得...