一种K2-x Mn8O16纳米线的制备方法技术
A preparation method of K2-x Mn8O16 nanowires
The invention provides a preparation method of K2 xMn8O16 nanowires. The method uses manganese sulfate and Potassium Permanganate as reactant to prepare a K2 xMn8O16 nanowire by one step of hydrothermal method, including the following steps: Step 1, prepare a mixed solution of manganese sulfate solution and Potassium Permanganate solution; step two, step one step The mixed solution is moved to the reaction kettle to get the product; step three, the product obtained by washing step two; step four, drying the products after washing, and obtaining the K2 xMn8O16 nanowires. The method does not require the introduction of surfactants, does not need to adjust the pH value, and is simple and convenient to operate. The purity of K2 xMn8O16 nanowires prepared is high.
【技术实现步骤摘要】
一种K2-xMn8O16纳米线的制备方法
本专利技术涉及过渡金属化合物纳米材料
，尤其涉及一种K2-xMn8O16纳米线的制备方法。
技术介绍
锰，化学符号是Mn,原子序数为25，在元素周期表中位于第四周期，第VIIB族，属于比较活泼的金属，是一种灰白色、硬脆，有光泽的过渡金属，其在化合物中的化合价主要包括+2、+3、+4、+5、+6和+7，这也就意味着含锰氧化物或化合物的种类繁多，如水钠锰矿、钙锰矿、黑锰矿、隐钾锰矿等等。其中，隐钾锰矿因其具有特殊的物理化学性质而吸引了大量研究人员的关注，该锰矿广泛存在于自然界中，如土壤、海洋等，但均具有相同的结构单元，即锰氧八面体。本专利技术涉及的K2-xMn8O16纳米线属于纳米材料范畴，因其尺寸在纳米尺度范围而具有诸如比表面积大、离子交换能力强等优点，进而在二次电池电极材料、离子交换、吸附等领域均具有重要的应用价值和前景。
技术实现思路
本专利技术提供了一种K2-xMn8O16纳米线的制备方法，在该方法中，以硫酸锰和高锰酸钾试剂的混合水溶液，然后利用水热法即可得到K2-xMn8O16纳米线，方法简单易行，没有引入其他物质...
【技术保护点】
一种K2‑xMn8O16纳米线的制备方法，其特征在于，该方法以硫酸锰和高锰酸钾作为反应物，通过水热法一步制备得到K2‑xMn8O16纳米线，包括以下步骤：步骤一，配制硫酸锰溶液和高锰酸钾溶液的混合溶液；步骤二，将步骤一得到的混合溶液移至反应釜中反应得到产物；步骤三，洗涤步骤二得到的产物；步骤四，将洗涤后的产物烘干，得到K2‑xMn8O16纳米线。
【技术特征摘要】
1.一种K2-xMn8O16纳米线的制备方法，其特征在于，该方法以硫酸锰和高锰酸钾作为反应物，通过水热法一步制备得到K2-xMn8O16纳米线，包括以下步骤：步骤一，配制硫酸锰溶液和高锰酸钾溶液的混合溶液；步骤二，将步骤一得到的混合溶液移至反应釜中反应得到产物；步骤三，洗涤步骤二得到的产物；步骤四，将洗涤后的产物烘干，得到K2-xMn8O16纳米线。2.根据权利要求1所述的一种K2-xMn8O16纳米线的制备方法，其特征在于，所述配制的硫酸锰溶液的浓度为：0.006mol/L～0.01mol/L。3.根据权利要求1所述的一种K2-xMn8O16...
【专利技术属性】
技术研发人员：董立峰，张乾，吴祥芳，张晴晴，董红周，隋静，杨丰键，王玉博，
申请(专利权)人：青岛科技大学，
类型：发明
国别省市：山东,37