还原氧化石墨烯、四氧化三铁和聚苯胺的三元纳米复合材料制备方法及应用技术
Preparation and application of three yuan nanocomposites for reduction of graphene oxide, iron oxide and polyaniline
The preparation method and application of the three element nano composite material for reducing the graphene oxide, iron oxide and polyaniline, and the preparation technology of the functional nano anticorrosion composite used for the waterborne anticorrosion coating material. The redox reaction and oxidation polymerization of graphene oxide, iron oxide and aniline are used to form nanocomposites with electron transfer interaction between three elements. The mass ratio of graphene oxide, iron oxide and aniline is 3: 4~7: 6~24. The three element nanocomposites are filled in water-based coating resin to prepare water-based nano coatings. It is found that the water coating coating has better corrosion resistance than the unfilled nano composite coating. The three component nanocomposites are highly efficient anticorrosive mechanisms, high barrier properties of nanocomposites and passivation of metal surfaces.
【技术实现步骤摘要】
还原氧化石墨烯、四氧化三铁和聚苯胺的三元纳米复合材料制备方法及应用
本专利技术涉及用于水性防腐涂层材料的功能纳米防腐复合材料的制备
技术介绍
金属腐蚀是指金属和它所处的环境介质之间发生化学、电化学或物理作用，引起金属的变质和损坏。金属的腐蚀给整个社会带来巨大的损失，如何减轻金属腐蚀已经成为备受人们关注的问题。据统计，全世界每年因为腐蚀而被破坏的钢铁达总量的1/3以上，不可回收利用的金属腐蚀物达到总量的1/9，这造成资源的巨大浪费。另一方面，金属设备的腐蚀会给生产、生活带来较大的安全隐患，例如化工设备发生腐蚀易导致设备穿孔引发化学原料泄露，从而引起爆炸和有毒物质扩散，给生产工人和周边居民以及环境造成极大的危害。因此，各国研究人员设法研究以减缓和阻止腐蚀的发生。目前经济适用的金属防腐方法是在金属表面涂覆防腐涂料，以延长金属使用寿命。传统防腐涂料设计原理大多采用富锌底漆，富锌底漆的锌粉设计浓度不低于防腐涂料的70%（重量），才能实现牺牲阳极保护阴极（金属基材），或采用铬、镍等有毒重金属在金属基材表面形成致密的金属络合物，实现防腐。上述方案不是造成资源的过度消耗...
【技术保护点】
还原氧化石墨烯、四氧化三铁和聚苯胺的三元纳米复合材料的制备方法，由氧化石墨烯、四氧化三铁和苯胺经还原反应以及原位氧化聚合反应，形成三元界面间具有电子转移相互作用的纳米复合材料，其特征在于：所述氧化石墨烯、四氧化三铁和苯胺的投料质量比为3∶4～7∶6～24。
【技术特征摘要】
1.还原氧化石墨烯、四氧化三铁和聚苯胺的三元纳米复合材料的制备方法，由氧化石墨烯、四氧化三铁和苯胺经还原反应以及原位氧化聚合反应，形成三元界面间具有电子转移相互作用的纳米复合材料，其特征在于：所述氧化石墨烯、四氧化三铁和苯胺的投料质量比为3∶4～7∶6～24。2.权利要求1所述还原氧化石墨烯、四氧化三铁和聚苯胺的三元纳米复合材料的制备方法，先将氧化石墨烯和四氧化三铁在超声条件下分散到水中，加入苯胺后，在95℃条件下反应，得到苯胺还原的氧化石墨烯负载Fe3O4二元复合材料；反应结束后，将反应...