一种净尺寸工字型结构的制备方法技术
A preparation method of net size structure
The invention is a preparation method of a net size type structure. The preparation method comprises the following steps: (A) preparing the preform mold and the upper and lower main dies; (B) placing two parts of the C structure in the preform mold and pruning to the net size; (C) a prepreg and a flanging are laid on the main die of (C). (D) the C type structure preform is covered with the upper and lower main dies respectively, then the die is closed and the flanging is turned; (E) is laid on the citron section, and the silicone rubber strips are used to cover and compacted; (F) the air felt and vacuum bags are covered and the vacuum bag is pressed and solidified. The invention adopts the preform mold to improve the efficiency of the structure forming. At the same time, the net size forming method can be applied to the overall structure of some composite materials directly, and effectively evade the processing risk.
【技术实现步骤摘要】
一种净尺寸工字型结构的制备方法
本专利技术涉及一种净尺寸工字型结构的制备方法。
技术介绍
目前复合材料工字型结构制备，普遍采用对橼条后加工的方式以达到要求尺寸，增加橼条分层风险的同时，降低了结构成型效率。
技术实现思路
为了解决上述问题，本专利技术提供了一种净尺寸工字型结构制备方法，解决现有技术中存在的橼条分层风险，提高产品使用寿命及成型效率。为了达到上述目的，本专利技术是通过以下技术方案实现的：本专利技术是一种净尺寸工字型结构的制备方法，制备方法包括如下步骤：（A）准备预制体模具及上下主模具；（B）在预制体模具铺贴两部分C型结构，并修剪至净尺寸，得C型预制体模具；（C）上下的所述主模具上分别铺贴一层预浸料，留出翻边；（D）将C型结构预制体分别铺覆于上下的所述主模具上，随后进行合模，并翻起翻边；（E）铺贴橼条部分，并使用硅橡胶条覆盖压实；（F）包覆透气毡及真空袋，真空袋压固化成型。本专利技术的进一步改进在于：在步骤（A）中所述预制体模具与所述主模具成型面尺寸宽度一致，高度相差一层预浸料的厚度，且主模具设有限位孔。本专利技术的有益效果是：本专利技术采用预制体模具，提高了...
【技术保护点】
一种净尺寸工字型结构的制备方法，其特征在于：所述制备方法包括如下步骤：（A）准备预制体模具及上下主模具（4）；（B）在预制体模具铺贴两部分C型结构，并修剪至净尺寸，得C型预制体模具（3）；（C）上下的所述主模具（4）上分别铺贴一层预浸料，留出翻边；（D）将C型结构预制体（5）分别铺覆于上下的所述主模具（4）上，随后进行合模，并翻起翻边；（E）铺贴橼条部分，并使用硅橡胶条（7）覆盖压实；（F）包覆透气毡及真空袋，真空袋压固化成型。
【技术特征摘要】
1.一种净尺寸工字型结构的制备方法，其特征在于：所述制备方法包括如下步骤：（A）准备预制体模具及上下主模具（4）；（B）在预制体模具铺贴两部分C型结构，并修剪至净尺寸，得C型预制体模具（3）；（C）上下的所述主模具（4）上分别铺贴一层预浸料，留出翻边；（D）将C型结构预制体（5）分别铺覆于上下的所述主模具（4）上...
【专利技术属性】
技术研发人员：张星星，王友聪，贾鹏军，张咪咪，
申请(专利权)人：江苏恒神股份有限公司，
类型：发明